Type-I silicon clathrates containing lithium

Bodo Böhme,Matej Bobnar,Alim Ormeci,Sarah Peters,Walter Schnelle,Michael Baitinger,Yuri Grin

DOI: https://doi.org/10.1515/zkri-2016-1983

2016-11-02

Abstract:Abstract The intermetallic phase [Li x Ba 8− x ][Li y Si 46− y ] is the first example of a clathrate-I silicide containing lithium with the peculiarity that the Li atoms occupy both cage and framework positions. The phase was obtained by ambient-pressure solid-state reactions at 400°C between Ba 4 Li 2 Si 6 and the binary clathrate phase Ba 8− x Si 46 applying different experimental approaches. In this reaction, Li atoms substitute Si atoms of the framework at site 6 c (space group Pm 3̅ n ) and fill up the Ba-deficient dodecahedral Si 20 cages at site 2 a . The presence of Li atoms in the clathrate phase was proven by combined X-ray powder diffraction, 7 Li and 29 Si solid-state NMR analyses. Incorporation of lithium markedly increased the lattice parameter of the clathrate phase, e.g. from a =10.3200(2) Å for Ba 7.48(2) Si 46 to a =10.3715(3) Å for [Li 0.59(2) Ba 7.41(2) ][Li 2.3(1) Si 43.7(1) ]. The critical temperature T c for the transition to the superconducting state decreased from 7.7 K to 3.2 K upon Li incorporation.