Thermal stability and thermal conductivity of stacked Cs intercalated layered niobate

Wenjuan Wang,Xiaosong Bai,Huiyu Yuan,Tingting Xu,Jinxing Gao,Junyan Cui,Daoyuan Yang,Chengliang Ma

DOI: https://doi.org/10.1016/j.ceramint.2023.07.151

IF: 5.532

2023-07-01

Ceramics International

Abstract:Layered materials exhibit competitively low thermal conductivity along the out-of-plane direction. The solution process is a promising method for preparing stacked structures. However, the thermal stability of the layered materials is poor after processing in solution, thus hindering their applications at high temperatures. One of the solutions to improve the thermal stability of layered structures is to expand the interlayer distance by inserting large-size metal ions. In this work, we studied the thermal properties of Cs+ intercalated layered niobate obtained by the ion-exchanged process. The layered structure of the Cs+ intercalated layered niobate survives after thermal treatment even at 1200 °C. The room temperature thermal conductivity of as prepared stacked Cs–HCa2Nb3O10 is as low as 0.11 W m−1 k−1. Upon thermal annealing, the thermal conductivity increases. After annealing at 1200 °C, the value is 0.90 W m−1 k−1. The finding suggests Cs+ intercalated layered niobate is a promising material for high-temperature insulation applications.

materials science, ceramics