Syntheses and properties of novel polyarylates with ethyl units as a side group

Yu Zhang,Zheng Lei,Guang-ming Yan,Jie Yang,Gang Zhang

DOI: https://doi.org/10.1016/j.mtcomm.2021.102643

IF: 3.8

2021-09-01

Materials Today Communications

Abstract:<p>A series of polyarylates (PAHAs) with ethyl pendent groups were synthesized from 2,2-bis (4-hydroxyphenyl) propane, bisphenol and two different benzenedicarbonyl chlorides through interfacial copolymerization. The structures and aggregation states of the copolymers were confirmed by FT-IR, ¹H NMR and XRD. The resultant polyarylates have excellent thermal properties with the glass transition temperature of 196.2–196.9 °C and the 5% mass loss temperature of 437.6–458.5 °C. Because of the introduction of ethyl pendent groups, the transmittance at 400 nm and 450 nm of polymer films can reach up to 84.86–85.20% and 85.75–86.52%. The cut-off wavelength was in the range of 309–314 nm, lower than that of commercial product U-100. The results of rheology properties testing suggest the viscosity of PAHAs decreased from 16720 to 617.1 Pa·s under 285–310 °C with the incorporation of ethyl pendent groups. Meanwhile, when the test time was extended to 30 min at 310 °C, the complex viscosity of PAHAs had almost no change, indicating the exceptional melt flowability and stability of polyarylates PAHAs. That is beneficial for the application of its melt process such as injection molding, especially for thin wall products.</p>

materials science, multidisciplinary