Preparation, Air Filtration Performance of a Fluorinated Polyimide/Polyacrylonitrile Nanofibrous Membrane by Electrospinning

Chen Chen,Lulu Xiong,Yahui Cui,Chaosheng Wang
DOI: https://doi.org/10.3390/polym16091240
IF: 5
2024-04-30
Polymers
Abstract:This paper reports the successful fabrication of a new nanofibrous membrane, F-PI/PAN, through electrospinning of polyacrylonitrile (PAN) and fluorinated polyimide (F-PI). The nanofibrous membrane exhibits comprehensive properties for high-temperature filtration and robust PM2.5 (particulate matter with an aerodynamic equivalent diameter of 2.5 microns or less) removal. The introduction of F enhances the hydrophobicity of the PI. The relationship between the hydrophobic performance and the filtration performance of particles is investigated. The chemical group of the composite membrane was demonstrated using FITR, while the surface morphology was investigated using field emission scanning electron microscopy. The TGA results indicated good thermal stability at 300 °C. Various ratios of F-PI membranes were prepared to characterize the change in properties, with the optimal mass ratio of F-PI being 20 wt%. As the proportion of F-PI increases, its mechanical and filtration efficiency properties and hydrophobicity become stronger. The contact angle reaches its maximum of 128 ± 5.2° when PAN:F-PI = 6:4. Meanwhile, when PAN:F-PI = 8:2, the filtration efficiency reaches 99.4 ± 0.3%, and the elongation at break can reach 76%. The fracture strength can also reach 7.1 MPa, 1.63 times that of the pure PAN membrane.
polymer science
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to develop an air - filtering material that is efficient, durable and has good filtering performance in order to deal with the increasingly serious air pollution problem. Specifically, the author prepared a new type of fluorinated polyimide / polyacrylonitrile (F - PI / PAN) nanofiber membrane by electrospinning technology and studied its performance in high - temperature filtering and fine particulate matter (such as PM 2.5) removal. ### Main problems and solutions 1. **Improve filtering efficiency**: - Research shows that although the existing air - filtering materials have a certain filtering effect, there is still room for improvement in terms of high filtering efficiency, low energy consumption and long service life. For this reason, the author introduced fluorinated polyimide (F - PI) and compounded it with polyacrylonitrile (PAN) to improve the comprehensive performance of the filtering membrane. 2. **Enhance hydrophobicity**: - Fluorine atoms have extremely high electronegativity and can significantly improve the hydrophobic performance of materials. Therefore, the author improved the hydrophobicity of polyimide by introducing fluorinated groups, thereby enhancing the trapping ability of the filtering membrane for particulate matter. 3. **Optimize mechanical properties and thermal stability**: - By adjusting the ratio of F - PI to PAN, the author found that as the F - PI content increased, the mechanical strength and thermal stability of the composite membrane also improved. For example, when the mass ratio of F - PI was 20 wt%, the composite membrane exhibited the best comprehensive performance. ### Experimental methods To verify the above hypotheses, the author carried out the following experiments: - **Material preparation**: Prepare F - PI / PAN nanofiber membranes with different ratios by electrospinning technology. - **Performance testing**: Include tests on filtering efficiency, pressure drop, contact angle, thermal stability and mechanical properties. - **Characterization means**: Use instruments such as FTIR, SEM, TGA to characterize in detail the chemical structure, microscopic morphology and thermal stability of the composite membrane. ### Results summary The experimental results show that as the F - PI content increases, the filtering efficiency, hydrophobicity and mechanical properties of the composite membrane all improve. In particular, when the mass ratio of F - PI to PAN is 8:2, the filtering efficiency reaches 99.4 ± 0.3%, and the elongation at break can reach 76%, which is much higher than the performance of the pure PAN membrane. In addition, the composite membrane also shows good thermal stability and can still maintain stable performance at 300 °C. In conclusion, this research has successfully developed a high - performance F - PI / PAN nanofiber membrane, providing a new and effective way to solve the air pollution problem.