Abstract:A facile confinement approach coupled with mixed‐valence‐state strategy is introduced to confine carbon intermediates, which subsequently cover the local catalyst surface and stabilize Cu+ species. As a result, the mixed‐valence‐state Cu2O/CuO catalysts yields multi‐carbon (C2+) products with a Faradaic efficiency (FE) of 80.0 % at a C2+ partial current density of 320.0 mA cm−2 and shows superior stability exceeding 30 h in membrane electrode assembly (MEA) electrolyser. Copper oxide nanomaterials have been suggested to be efficient for highly selective multi‐carbon (C2+) production in CO2 reduction reaction (CO2RR), due to the introduction of surface Cu+ species from oxide catalysts. However, the Cu+ species on the catalyst surface are prone to being reduced to Cu0 under reductive conditions during CO2RR. Here, a network‐structured catalyst is developed consisting of ultrafine Cu2O/CuO nanoparticles that harbor an abundance of pores. This catalyst is synthesized via flame spray pyrolysis (FSP) method and engineered to confine carbon intermediates, which subsequently cover the local catalyst surface and stabilize Cu+ species. As a result, a C2+ products Faradaic efficiency (FE) of approximately 80.0% at a partial current density of 320.0 mA cm−2 is achieved, and a large C2+ to C1 ratio of ≈9.7. In situ XRD and XPS spectra are employed to reveal the indeed presence of Cu+ species on the catalyst surface during the CO2RR process, which extensively improves the adsorption of *CO intermediates and thus the C─C coupling reaction to form C2+ products.

Pyrolysis-free synthesis of high-loading single-atomic Cu catalyst for efficient electrocatalytic CO2-to-CH4 conversion

Pyrolysis-free Synthesis of a High-Loading Single-Atom Cu Catalyst for Efficient Electrocatalytic CO2-to-CH4 Conversion.

Superaerophilic Copper Nanowires for Efficient and Switchable CO2 Electroreduction.

Highly selective conversion of carbon dioxide to methane by copper single atom electrocatalysts

Energy-efficient CO(2) conversion to multicarbon products at high rates on CuGa bimetallic catalyst

Nitrogen-Adsorbed Hydrogen Species Promote CO 2 Methanation on Cu Single-Atom Electrocatalyst

Atomic Cu Sites Engineering Enables Efficient CO2 Electroreduction to Methane with High CH4/C2H4 Ratio

Nitrogen-Adsorbed Hydrogen Species Promote CO2 Methanation on Cu Single-Atom Electrocatalyst

Stabilizing Cu+ Species in Cu2O/CuO Catalyst via Carbon Intermediate Confinement for Selective CO2RR

Self‐supporting Copper‐based Electrode by Electrospinning for Reduction of Carbon Dioxide to Methane

MOF Encapsulating N-Heterocyclic Carbene-Ligated Copper Single-Atom Site Catalyst towards Efficient Methane Electrosynthesis

Fabrication of Cu-CeO2 Catalyst with Abundant Interfacial Cu+-O-Ce3+-OV (oxygen Vacancy) Sites for Boosting CO2 Electroreduction to Methane

Cold plasma activated Cu–Co multi-active centers tandem catalysts for efficient electrocatalytic CO2 into C2H4

Lowering *CO Affinity over Cu Nanoparticles for Enhanced Electrochemical CO 2 Conversion to Multi-Carbon Products at High Current Density

Direct Low Concentration CO2 Electroreduction to Multicarbon Products Via Rate-Determining Step Tuning

Graphdiyne enables Cu nanoparticles for highly selective electroreduction of CO 2 to formate

Efficient Electromethanation from CO 2 on Monodisperse Cu-Based Catalysts

Enriching the Local Concentration of CO Intermediates on Cu Cavities for the Electrocatalytic Reduction of CO2 to C2+ Products.

Boosting CO2 electrocatalytic reduction to ethylene via hydrogen-assisted C-C coupling on Cu2O catalysts modified with Pd nanoparticles

Molecular Modulation of Sequestered Copper Sites for Efficient Electroreduction of Carbon Dioxide to Methane

Atmosphere Induces Tunable Oxygen Vacancies to Stabilize Single-Atom Copper in Ceria for Robust Electrocatalytic CO2 Reduction to CH4