Rheological response of shear thickening fluid reinforced with silicon nitride nanoparticles

Minghai Wei,Kun Lin,Jiapeng Qi

DOI: https://doi.org/10.1007/s12034-024-03269-2

IF: 1.878

2024-07-18

Bulletin of Materials Science

Abstract:In this study, we studied the shear thickening performance of a novel silicon nitride and silica-mixed nanoparticles suspension. Silicon-nitride/silica-shear thickening fluids (Si 3 N 4 /SiO 2 -STFs) with different mass fraction ratios were prepared using polyethylene glycol as a dispersion medium. For the Si 3 N 4 /SiO 2 -STFs, the results showed that the viscosity increased from 168.35 (0.0 wt% Si 3 N 4 ) to 1387.73 Pa s (7.5 wt% Si 3 N 4 ), and a concomitant decrease in the critical shear rate from 10.0 to 3.55 s –1 , while thickening period decreased from 60.92 to 16.03 s –1 . Dynamic rheological analysis showed that compared with SiO 2 -based STF (SiO 2 -STF), the peak values of storage and loss modulus of 7.5%Si 3 N 4 /20%SiO 2 -STF (7.5 wt% Si 3 N 4 and 20 wt% SiO 2 ) increased nearly six times and three times, respectively. The results also showed that, compared with SiO 2 -STF, the thickening ratio of 7.5%Si 3 N 4 /20%SiO 2 -STF increases by 174% at 45°C and slows down the effect of temperature increase on the thickening period. This work provides a novel method for high-performance STF.

materials science, multidisciplinary