Investigation of polyurethane-based pressure-sensitive adhesives with castor oil as a polyol

Jian Huang,Anlong Li,Kaichang Li

DOI: https://doi.org/10.1016/j.ijadhadh.2020.102763

IF: 3.848

2021-03-01

International Journal of Adhesion and Adhesives

Abstract:<p>Renewable castor oil (CO) was investigated as a polyol for preparation of polyurethane-based pressure sensitive adhesives (PSAs). PSAs from the one-pot reaction of CO, poly(propylene glycol) (PPG), toluene diisocyanate (TDI) and DBTDL have all desirable properties for applications as surface protective films. NCO-terminated PPG-TDI adducts were prepared from reactions of PPG and TDI at room temperature (as designated as PPG-TDI_R) and 100 °C (as designated as PPG-TDI₁₀₀), respectively. The PSAs from reactions of CO and PPG-TDI_R or PPG-TDI₁₀₀ had higher peel strengths than those from reactions of CO and the mixture of PPG and TDI. PPG-TDI_R resulted in a higher peel strength of the resulting PSAs than PPG-TDI₁₀₀. A two-stage curing process of the partial curing of the mixture of CO and PPG-TDI_R at 125 °C and the final curing in an ambient environment was better than one-stage complete curing at 125 °C in terms of enhancing the peel strength of the resulting PSAs. The NCO/OH molar ratio of 0.85 in the mixture of CO and PPG-TDI_R resulted in the highest peel strength for the PSAs from CO and PPG-TDI_R. The PSAs from CO and PPG-TDI_R had good aging resistance and can be tailored for various applications such as labels and tapes. PPG was superior to poly(ethylene glycol) (PEG) in terms of enhancing the peel strength of the resulting PSAs. The curing mechanisms are discussed in detail.</p>

materials science, multidisciplinary,engineering, chemical