Aliphatic Polycarbonate-Based Binders for High-Loading Cathodes by Solvent-Free Method Used in High Performance LiFePO4|Li Batteries

Bin Chen,Zhe Zhang,Change Wu,Sheng Huang,Min Xiao,Shuanjin Wang,Hui Guo,Dongmei Han,Yuezhong Meng

DOI: https://doi.org/10.3390/ma17133153

IF: 3.4

2024-06-28

Materials

Abstract:The binder ratio in a commercial lithium-ion battery is very low, but it is one of the key materials affecting the battery's performance. In this paper, polycarbonate-based polymers with liner or chain extension structures are proposed as binders. Then, dry LiFePO4 (LFP) electrodes with these binders are prepared using the solvent-free method. Polycarbonate-based polymers have a high tensile strength and a satisfactory bonding strength, and the rich polar carbonate groups provide highly ionic conductivity as binders. The batteries with polycarbonate-based polymers, PPC-P, as binders were shown to have a long cycle life (350 cycles under 1 C, 89% of capacity retention). The preparation of dry electrodes using polycarbonate-based polymers can avoid the use of solvents and shorten the process of preparing electrodes. It can also greatly reduce the manufacturing cost of batteries and effectively use industrial waste gas dioxide oxidation. Most importantly, a battery material with this kind of polycarbonate polymer as a binder is easily recycled by simply heating after the battery is discarded. This paper provides a new idea for the industrialization and development of a novel binder.

materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter

What problem does this paper attempt to address?

The paper mainly discusses the use of aliphatic polycarbonate as a binder in lithium-ion batteries. Traditionally, polyvinylidene fluoride (PVDF) is commonly used as a binder in commercial lithium-ion batteries. However, it has issues such as the need for organic solvents, insufficient ion conductivity, and environmental and safety concerns during the recycling process. To address these issues, the researchers proposed using polycarbonate-based polymers to prepare high-loading cathodes for high-performance LiFePO4|Li batteries using a solvent-free method.

These polycarbonate-based polymers have high tensile strength and good adhesion. Their rich polar carbonate groups provide high ion conductivity. The preparation of dry electrodes using a solvent-free method avoids the use of solvents, reduces production time and energy consumption, and lowers battery manufacturing costs. In addition, these polymers have flowability at high temperatures, which facilitates uniform dispersion between electrode materials during the hot pressing step, suitable for dry electrodes. Moreover, they can be easily recovered by simple heating after battery disposal, as they decompose into carbon dioxide and water at 400℃.

The paper demonstrates through comparative experiments that polycarbonate-based polymers, such as PPC-P, as binders, exhibit better electrochemical performance in batteries, including longer cycle life (89% capacity retention after 350 cycles at 1C). Furthermore, the study evaluates the effects of different structures of polycarbonate polymers on battery performance.

In conclusion, this paper aims to address the issues of environmentally friendly, efficient, and recyclable binders in lithium-ion batteries and proposes a new strategy using polycarbonate-based polymers, providing innovative ideas for battery manufacturing and recycling.