Abstract:Over recent years, new interstitial free (IF) steel grades containing controlled low levels of carbon and nitrogen have been adopted to fabricate car body panels. The processing and properties of these steels are reviewed. They can provide very high levels of formability, as indicated by width to thickness strain ratios during forming r of 1.8 (r values of traditional aluminium killed steels rarely exceed 1.8). Typically total interstitial contents are in the region <0.0030 wt-%C and <0.0040 wt-%N. Elimination of these solutes damaging to formability is achieved through careful control of the melt chemistry during steelmaking and by the hyperstoichiometric addition of titanium and/or niobium to react with carbon and nitrogen to form precipitates. Precipitation control during hot mill processing is instrumental in determining the grain size of the hot rolled material, which must be as small as possible, and grain size in the final cold rolled and annealed product, which must be optimised for formability. Control of crystallographic texture is also fundamental in producing exceptional deep drawability. Subsequent casting, rolling, and annealing operations must also be controlled to optimise the development of preferred precipitation and texture. The chemistry is designed such that under equilibrium conditions IF steel should contain no carbon or nitrogen in solid solution. Hot rolling, however, is a process in which equilibrium is not attained, and for this reason it is desirable for the removal of carbon and nitrogen to begin early in the hot rolling process. The most favourable removal mechanism in this respect is the precipitation of titanium carbosulphide (titanium carbide and niobium carbide also proliferate, but precipitate out at lower temperatures). Titanium carbosulphide formation is favoured when the slab reheat temperature is <1200°C, and when the C/S ratio approaches stoichiometric. Optimum finishing temperatures are close to the Ar 3 temperature but practically it is advisable to increase the finishing temperature by 20–30 K above Ar 3 to avoid the risk of ferritic rolling taking place at the edges of the strip. For high formability in the final product, fast cooling on the runout table is required to prevent excessive grain growth. For titanium only containing IF steels, coiling temperature dependency is small; thus the favoured coiling temperature is low (∼625°C) to obviate the need for aggressive scale removal techniques. Coiling temperature dependence in niobium containing IF steels is greater, and precipitate coarsening is required to aid recrystallisation during annealing, which may be carried out at up to 50 K higher than in titanium IF steels; thus coiling temperatures are usually >700°C. High reductions, up to approximately 90%, in the cold mill are the key to deep drawability. Annealing temperature is instrumental in determining final drawability providing the Ac 3 temperature has not been exceeded. Time at temperature is also an important factor enabling grain growth to occur, optimising formability.

Effect of Ti on Formability of IF Steels

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Influence of Ti content on mechanical properties of low carbon steel

Effect of Mn and P on the macroscopic texture of Ti-Nb stabilized interstitial free steels

Processing and properties of mild interstitial free steels

Effect of Titanium Addition on As-Cast Structure and High-Temperature Tensile Property of 20Cr-8Ni Stainless Steel for Heavy Castings

Effect of Ti Addition on Yield Strength of Low‐Mo Fire‐Resistant Steel at Elevated Temperatures

Effect of Microstructure on Strain-hardening Behaviour of a Ti-IF Steel Grade

Effect of Fe content on microstructure and hardness of Ti-4.5Mo–5Al-1.8Zr-2.5Cr-1.1Sn titanium alloy based on high-throughput diffusion couple

Precipitation Behavior of Ti in High Strength Steels

Effect of Ti and S Content on the Properties and Machinability of Low-Carbon Ferritic–Pearlitic Steel

Effect of Ti content on microstructures and mechanical properties of cast Al-2Li-2Cu-0.5Mg alloy

Textures and Precipitates in A 17%cr Ferritic Stainless Steels

Effect of Ti content on microstructure and properties of Al-9.9Zn-2.6Mg-0.91Cu-0.2Zr-xTi aluminum alloy

Effect of Magnesium Content on Precipitation Behavior of TiN-Containing Inclusions in High-Titanium High-Strength Steel

Microstructure, Texture, and Formability of Nb+Ti Stabilized High Purity Ferritic Stainless Steel

The Influence of the Hot-Rolling Temperature on the Microstructure and Mechanical Properties of Ti-Nb Microalloyed 21%Cr Ferritic Stainless Steel

Effect of titanium content on the precipitation behavior of carbon-saturated molten pig iron

Effect of Zr Treatment on Inclusion and Solidification Microstructure in Ti Deoxidized Low Carbon Microalloyed Steel

Effect of Multidirectional Isothermal Forging on Microstructure and Mechanical Properties in Ti-6Al-4V Alloy

The investigation of precipitation behavior of titanium compounds for high titanium steel based on in situ observation