Identification of the Active-Layer Structures for Acidic Oxygen Evolution from 9R-BaIrO 3 Electrocatalyst with Enhanced Iridium Mass Activity

Na Li,Liang Cai,Chao Wang,Yue Lin,Jinzhen Huang,Hongyuan Sheng,Haibin Pan,Wei Zhang,Qianqian Ji,Hengli Duan,Wei Hu,Wenhua Zhang,Fengchun Hu,Hao Tan,Zhihu Sun,Bo Song,Song Jin,Wensheng Yan
DOI: https://doi.org/10.1021/jacs.1c04087
IF: 15
2021-10-25
Journal of the American Chemical Society
Abstract:Iridium-based perovskites show promising catalytic activity for oxygen evolution reaction (OER) in acid media, but the iridium mass activity remains low and the active-layer structures have not been identified. Here, we report highly active 1 nm IrO<sub><i>x</i></sub> particles anchored on 9R-BaIrO<sub>3</sub> (IrO<sub><i>x</i></sub>/9R-BaIrO<sub>3</sub>) that are directly synthesized by solution calcination followed by strong acid treatment for the first time. The developed IrO<sub><i>x</i></sub>/9R-BaIrO<sub>3</sub> catalyst delivers a high iridium mass activity (168 A g<sub>Ir</sub><sup>-1</sup>), about 16 times higher than that of the benchmark acidic OER electrocatalyst IrO<sub>2</sub> (10 A g<sub>Ir</sub><sup>-1</sup>), and only requires a low overpotential of 230 mV to reach a catalytic current density of 10 mA cm<sup>-2</sup><sub>geo</sub>. Careful scanning transmission electron microscopy, synchrotron radiation-based X-ray absorption spectroscopy, and X-ray photoelectron spectroscopy analyses reveal that, during the electrocatalytic process, the initial 1 nm IrO<sub><i>x</i></sub> nanoparticles/9R-BaIrO<sub>3</sub> evolve into amorphous Ir<sup>4+</sup>O<sub><i>x</i></sub>H<sub><i>y</i></sub>/IrO<sub>6</sub> octahedrons and then to amorphous Ir<sup>5+</sup>O<sub><i>x</i></sub>/IrO<sub>6</sub> octahedrons on the surface. Such high relative content of amorphous Ir<sup>5+</sup>O<sub><i>x</i></sub> species derived from trimers of face-sharing IrO<sub>6</sub> octahedrons in 9R-BaIrO3 and the enhanced metallic conductivity of the Ir<sup>5+</sup>O<sub><i>x</i></sub>/9R-BaIrO<sub>3</sub> catalyst are responsible for the excellent acidic OER activity. Our results provide new insights into the surface active-layer structure evolution in perovskite electrocatalysts and demonstrate new approaches for engineering highly active acidic OER nanocatalysts.
chemistry, multidisciplinary
What problem does this paper attempt to address?
The paper attempts to address the problem of developing acidic oxygen evolution reaction (Oxygen Evolution Reaction, OER) catalysts with higher iridium mass activity and long-term electrochemical stability. Specifically, the study aims to improve the catalytic performance of iridium-based catalysts in acidic media by synthesizing 1 nm IrOₓ particles anchored on 9R-BaIrO₃. ### Background and Problem 1. **Importance of Electrochemical Water Splitting**: - Electrochemical water splitting plays a key role in clean energy technologies, but the slow oxygen evolution reaction (OER) at the anode limits its performance and industrial application. 2. **Limitations of Existing Catalysts**: - Currently, iridium oxides (such as IrO₂ or IrOₓ) are the best OER catalysts in acidic media in terms of activity and stability, but their high cost and scarcity limit practical applications. - Iridium-based perovskite oxides (such as 3C-SrIrO₃ and 6H-SrIrO₃) have shown enhanced catalytic activity and stability in acidic OER, but their surface active layer structure has not been verified. 3. **Research Objectives**: - Develop new iridium-based OER catalysts with higher iridium mass activity and long-term electrochemical stability in acidic media. - Systematically reveal the evolution process of the surface active layer nanostructure of iridium-based perovskite electrocatalysts. ### Main Contributions 1. **Synthesis and Characterization of Catalysts**: - A catalyst with 1 nm IrOₓ particles uniformly anchored on 9R-BaIrO₃ (IrOₓ/9R-BaIrO₃) was directly synthesized through solution calcination and strong acid treatment. - This catalyst exhibited high iridium mass activity (168 A gIr⁻¹) in acidic media, approximately 16 times higher than the benchmark catalyst IrO₂ (10 A gIr⁻¹). - It required a low overpotential of only 230 mV to achieve a catalytic current density of 10 mA cm⁻² and showed good electrochemical stability. 2. **Evolution of Surface Active Layer Structure**: - The evolution of the surface active layer structure during the electrocatalytic process was systematically revealed through scanning transmission electron microscopy (STEM), synchrotron radiation X-ray absorption spectroscopy (XAS), and X-ray photoelectron spectroscopy (XPS). - The initial 1 nm IrOₓ nanoparticles/9R-BaIrO₃ evolved into amorphous Ir⁴⁺Oₓ/IrO₆ octahedra during the electrocatalytic process, eventually forming amorphous Ir⁵⁺Oₓ/IrO₆ octahedra. - These high relative content amorphous Ir⁵⁺Oₓ species and enhanced metal conductivity are the reasons for the excellent acidic OER activity of this catalyst. ### Conclusion This study successfully developed an acidic OER catalyst IrOₓ/9R-BaIrO₃ with high iridium mass activity and good electrochemical stability, and systematically revealed the evolution process of its surface active layer nanostructure. These results provide new insights and methods for designing efficient and stable acidic OER nanocatalysts.