Enhanced thermoelectric properties of poly(3,4‐ethylenedioxythiophene): Poly(styrenesulfonate)/copper phthalocyanine disulfonic acid composite films

Siqi Wu,Yihan Wang,Lizhi Hu,Qiang Yin,Kai Du,Qinjian Yin,Libin Huang
DOI: https://doi.org/10.1002/app.50883
IF: 3
2021-04-16
Journal of Applied Polymer Science
Abstract:<p>A series of poly(3,4‐ethylenedioxythiophene): poly(styrenesulfonate)/copper phthalocyanine disulfonic acid (PEDOT: PSS/CuPc‐[SO<sub>3</sub>H]<sub>2</sub>) composite films were prepared by using CuPc‐(SO<sub>3</sub>H)<sub>2</sub> as the dopant. EG treatment was applied to further improve the thermoelectric properties of PEDOT: PSS/CuPc‐(SO<sub>3</sub>H)<sub>2</sub> composites. Structural analyses indicated the strong π − π interactions existed between PEDOT: PSS and CuPc‐(SO<sub>3</sub>H)<sub>2</sub>, and led to more ordered regions in the composite films, and benefit the conductivity. CuPc‐(SO<sub>3</sub>H)<sub>2</sub> can greatly improve the thermoelectric properties of PEDOT: PSS/CuPc‐(SO<sub>3</sub>H)<sub>2</sub> composite films, which have a Seebeck coefficient of 13.2 μV K<sup>−1</sup> and a conductivity of 2.8 × 10<sup>5</sup> S/m with 20 wt% CuPc‐(SO<sub>3</sub>H)<sub>2</sub> at room temperature, and the corresponding power factor is 48.8 μW m<sup>−1</sup> K<sup>−2</sup>, which is almost 6.83 times higher than the PEDOT: PSS films without CuPc‐(SO<sub>3</sub>H)<sub>2</sub>.</p>
polymer science
What problem does this paper attempt to address?