1,4-Bis(2-(pyridin-4-yl)vinyl)naphthalene and Its Zinc(II) Coordination Polymers: Synthesis, Structural Characterization, and Selective Luminescent Sensing of Mercury(II) Ion
Wu-Xiang Li,Hong-Xi Li,Hai-Yan Li,Min-Min Chen,Yi-Xiang Shi,Jian-Ping Lang
DOI: https://doi.org/10.1021/acs.cgd.7b00575
IF: 4.01
2017-01-01
Crystal Growth & Design
Abstract:Solvothermal reactions of Zn(NO3)(2).6H(2)O with 1,4-bis(2-(pyridin-4-yl)vinyl)naphthalene (1,4-bpyvna) and 1,3,5-benzenetricarboxylic acid (1,3,5-H3BTC) (molar ratio = 1:1:1) at 120 degrees C in CH3CN/H2O (v/v = 1:2) afforded one three-dimensional (3D) coordination polymer [Zn-2(1,4-bpyvna)(1,3,5-HBTC)(2)(H2O)](n) (1). Similar reactions with the same three components at 140 degrees C in dimethylformamide (DMF)/CH3CN/H2O produced another 3D coordination polymer {[Zn-2(1,4-bpyvna)(1,3,5-BTC)(OH)].H2O}(n) (2) in 72% yield. When the molar ratio of Zn(NO3)(2).6H(2)O, 1,4-bpyvna, and 1,3,5-H3BTC was changed to 1:1:2, the analogous treatment at 140 degrees C yielded one one-dimensional coordination polymer {[Zn(1,3,5-HBTC)(2)-(H2O)] [1,4-bpyvna-H-2].CH3CN} (3, 1,4-bpyvna-H2 = 4,4'-((1,1)-naphthalene-1,4-diylbis (ethen e-2,1-diyl))bis (pyridin-1-ium)). Solvothermal reactions of Zn(NO3)(2).6H(2)O with equimolar 1,4-bpyvna and 1 or 2 equiv of 4,4'-oxidibenzoic acid (4,4'-H(2)OBA) at 120 degrees C in DMF/CH3CN/hexane resulted in the formation of {[Zn-2(1,4-bp-yvna)(4,4'-OBA)(2)]-0.5DMF-2.25H(2)O}(n) (4) and [[Zn-2(1,4-bpyvna)(4,4'-OBA)(2)].3DMF}(n) (5), respectively. Compounds 1-5 were characterized by elemental analysis, IR spectroscopy, powder X-ray diffraction, single-crystal X-ray diffraction, and thermogravimetric analysis. Upon addition of Hg2+ ions to the DMF solution of 1,4-bpyvna, remarkable changes in the absorbance and emissive spectra were observed, associated with color changes, which were easily identified by the naked eye. This ligand could serve as a chemoprobe with the detection limit of Hg2+ being 0.060 ppm. When solid 2 was added in the DMF solution containing Hg(NO3)(2), the emission color of 2 was also changed from blue to yellow, and its detection limit of Hg2+ was as low as 0.057 ppm. This compound can be reused for several cycles without evident efficiency decay. Compound 2 would be a promising sensitive naked -eye indicator for low-concentration Hg2+ with high sensitivity and selectivity.