Abstract:Solidified natural gas storage (SNG) using hydrate can provide environmentally friendly, highly compact and non explosive mode of NG storage at mild storage conditions. The efficient and rapid formation of natural gas hydrate is of great significance to the industrial application of SNG. In this work, in order to improve the gas storage capacity and absorption rate of CH4 hydrate, experiments were carried by adding expanded graphite (EG) with sodium dodecyl sulfate (SDS) with a pressure range of 5.0–8.0 MPa and a temperature of 273.2 K. The results indicate that EG can not only promote the formation of hydrate by promoting the nucleation of hydrate, but also accelerated the growth of hydrate by enhancing hydration heat transfer. EG system (0.05 wt%, 0.08 wt%, and 0.10 wt%) enabled faster hydrate formation than a liquid water system, with a content of 0.08 wt% optimal for the enhancement of hydrate formation. In the combination of EG (0.08 wt%) and SDS solution, EG + 0.03 wt% SDS system can improve the kinetics of hydrate formation to the greatest extent; the maximum gas storage capacity reached 190.4 STP/g H2O, and the maximum gas storage speed reached 20.84 cm3·g−1·min−1 at 273.2 K and 6 MPa. Compared with the SDS system, the maximum methane uptake and rates of EG + 0.03 wt% SDS system increased by 11.90% ~ 26.18% and 15.09% ~ 51.67% under different pressures respectively. At relatively low pressure, the hydrate can achieve a saturation of ~90% in EG + 0.03 wt% SDS system. On the other hand, compared with other carbon materials such as graphite and carbon nanotubes, the gas storage capacity and average gas storage rate of EG system were 1.12–1.37 times and 1.67–30.17 times higher, respectively, under similar temperature and pressure conditions. Therefore, a collaborative mode of enhancing gas concentration, nucleation site and heat transfer efficiency at the gas–liquid interface of hydrate reaction with only one material (EG) was proposed to promote the formation of hydrate. Further study on the promotion mechanism of EG and amplification experiments are expected to provide an effective way for the commercial application of SNG process in future work.

Eco-friendly hydrogels serving as water carriers for improving methane hydrate formation and dissociation processes

Promoted methane hydrate formation in -SO3--rich hydrogel clathrate

Kinetics of Methane Hydrate Formation in a 1200 Ml Unstirred Reactor for Natural Gas Storage

Preparation of a Hydrogel-Based Promoter for Methane Hydrate Formation: Effects of −SO 3 – Density on Promotion Efficiency

Research Methane Hydrate Meta-stable Property for Application to Natural Gas Storage and Transportation

Polymeric superabsorbent hydrogel-based kinetic promotion for gas hydrate formation

Promoting methane hydrate formation with expanded graphite additives: Application to solidified natural gas storage

Synergistic effect of alcohol polyoxyethylene ether sodium sulphate and copper foam on methane hydrate formation

Pyrolytic aerogels with tunable surface groups for efficient methane solidification storage via gas hydrates

Inhibition on methane hydrate formation by polyacrylate superabsorbent hydrogel

Facile and sustainable methane storage via clathrate hydrate formation with low dosage promoters in a sponge matrix

Enhanced formation of methane hydrate from active ice with high gas uptake

Novel hydrophobic associative copolymers for natural gas hydrate fracturing fluids

Synthesis of methane hydrate at ambient temperature with ultra-rapid formation and high gas storage capacity

The Promoting Effect and Mechanisms of Oxygen-Containing Groups on the Enhanced Formation of Methane Hydrate for Gas Storage

Modified balsa wood with natural, flexible porous structure for gas storage

Multi-cycle methane hydrate formation in micro droplets of gelatinous dry solution

Microscopic study on the key process and influence of efficient synthesis of natural gas hydrate by in situ Raman analysis of water microstructure in different systems with temperature drop

Advances in research and developments on natural gas hydrate extraction with gas exchange

Novel Vermiculite/tannic Acid Composite Aerogels with Outstanding CO2 Storage Via Enhanced Gas Hydrate Formation

Novel vermiculite/tannic acid composite aerogels with outstanding CO 2 storage via enhanced gas hydrate formation