Cr dopant regulating d-orbital electronic configuration of NiFe spinel oxide to improve oxygen evolution reaction in Zn-air battery
Shihui Liu,Yaofeng Shi,Fengqin Tang,Penggang Wei,Wenrui Huang,Jiapeng Wu,Suya Zhao,Jikui Zhu,Chunhui Shi,Libing Hu
DOI: https://doi.org/10.1016/j.jallcom.2024.174248
IF: 6.2
2024-03-27
Journal of Alloys and Compounds
Abstract:Significant advancements towards enhancing the catalytic activity of spinel ferrites in oxygen evolution reaction (OER) have been achieved, however, further studies are required on this regard. In this study, Cr-doped spinel ferrite (NiFe 2 O 4 ) embedded in N-doped C (Cr-NiFe 2 O 4 @NC) was synthesized via a high-temperature treatment using an NiFe Prussian blue analog as a precursor and K 2 Cr 2 O 7 as a Cr source. Owing to the strong octahedral site preference energy, Cr 3+ ions were successfully doped into octahedral sites and tailored the electronic configuration of NiFe 2 O 4 , as confirmed by XPS. The Cr-substituted Cr-NiFe 2 O 4 @NC exhibited the overpotential of 241 mV at 10 mA cm −2 , which was smaller than that of NiFe 2 O 4 @NC (266 mV) at the same current density. Meanwhile, the Tafel slope of Cr-NiFe 2 O 4 @NC (65.32 mV dec −1 ) was also lower than that of NiFe 2 O 4 @NC (86.96 mV dec −1 ). Therefore, the Cr substitution can improve the electrocatalytic OER performance of NiFe 2 O 4 @NC. In particular, an assembled rechargeable Zn-air battery using Cr-NiFe 2 O 4 @NC as the cathode catalyst afforded a high power density (61.1 mA cm −2 ) together with a high specific capacity (740 mA g −1 ). Amazingly, it could power light-emitting diodes, demonstrating its real-world application. Density functional theory calculations revealed that Cr ion doping led to electron transfer in NiFe 2 O 4 , resulting in a density of electronic states close to the Fermi level, which probably regulated the adsorption/desorption behaviors of oxygenate intermediates (*O and *OOH), thus promoting the reaction kinetics of the OER. This study provides a helpful basis for the development of spinel oxides with high electrocatalytic OER activity and durability via cation doping.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering