Abstract:This work elucidates the interactions between Re and hydrogen at γ/γ′ interfaces, enhancing the hydrogen-embrittlement resistance of nickel-based single-crystal superalloy (Ni-SX). The H-charged Ni-SX exhibits severe embrittlement characterized by the appearance of parallel dislocation slip bands and micro-cracks, which could be effectively mitigated through improving the Re content. The segregation behaviors of hydrogen at γ/γ′ interfaces, as captured by hydrogen microprint technique, significantly diminish interfacial cohesion strength by reducing the local atomic bonding strength. Detailed characterizations of bonding charge density highlight that Re plays a crucial role in reducing hydrogen embrittlement susceptibility by suppressing the hydrogen-induced degradation of bonding strength. The role of Re on hydrogen-embrittlement resistance of superalloys is investigated through tensile tests and first-principles calculations, revealing the suppressive effect of Re on hydrogen-induced decohesion behaviors at γ/γ′ interface.

What problem does this paper attempt to address?

The paper primarily explores the role of rhenium (Re) in nickel-based single crystal superalloys (Ni-SX superalloy), particularly how it affects hydrogen embrittlement resistance. The study combines experimental methods with first-principles calculations to reveal how the interaction between rhenium and hydrogen at the γ/γ' interface enhances the superalloy's resistance to hydrogen embrittlement. Specifically, the study designed two nickel-based single crystal superalloys with different rhenium contents (3Re and 5Re) and conducted the following work: 1. **Hydrogen absorption and distribution**: Using the hydrogen microprint technique (HMT), it was observed that hydrogen tends to accumulate at the γ/γ' interface, indicating that hydrogen atoms preferentially adsorb at these interfaces, potentially becoming weak areas for hydrogen embrittlement. 2. **Mechanism of rhenium**: First-principles calculations revealed that the presence of rhenium can inhibit hydrogen enrichment at the γ/γ' interface, thereby reducing the negative impact of hydrogen on the interfacial bonding strength. When rhenium atoms occupy specific positions, they can reduce the chemical attraction of hydrogen atoms, thus decreasing the tendency of hydrogen to accumulate at the interface. 3. **Mechanical performance tests**: Slow strain-rate tensile tests compared the mechanical performance differences of the two alloys before and after hydrogen charging. The results showed that increasing the rhenium content can effectively improve the superalloy's resistance to hydrogen embrittlement, especially under high hydrogen concentrations. 4. **Microstructure analysis**: Scanning electron microscopy (SEM) observed that the fracture surface of the 3Re alloy after hydrogen charging exhibited numerous parallel slip bands and planar cracks, while the 5Re alloy showed better toughness characteristics. This indicates that rhenium can effectively suppress hydrogen-induced plastic deformation and crack initiation. In summary, the paper aims to explore how rhenium enhances the resistance of nickel-based single crystal superalloys to hydrogen embrittlement by altering hydrogen behavior at the γ/γ' interface. This finding is significant for developing a new generation of high-temperature structural materials, such as turbine blades for aircraft engines, with higher reliability and longer service life.

Interactions of Re and hydrogen at γ/γ′ interfaces enhanced hydrogen-embrittlement resistance of Re-optimized Ni-based superalloy

Hydrogenated vacancy induced changes in thermodynamic stability and mechanical properties of Re-containing γ-Ni/γ'-Ni 3 Al phase interface

Re Segregation at Interfacial Dislocation Network in a Nickel-Based Superalloy

Unveiling the Re segregation at γ/γ′ interface in Ni-based superalloy

Effect of Re in Gamma Phase, Gamma ' Phase and Gamma/Gamma ' Interface of Ni-Based Single-Crystal Superalloys

Insights into the effect of γ′- or γ′′-precipitated phase types on resistance against harmful atoms of heterogeneous interface in nickel-based superalloys

Influence of hydrogen behaviors on tensile properties of equiatomic FeCrNiMnCo high-entropy alloy

First‐Principle Calculation of the Hydrogen Adsorption and Diffusion Characteristics at an Ni3Al/Ni Interface

The Effects of Key Elements Re and Ru on the Phase Morphologies and Microstructure in Ni-based Single Crystal Superalloys

The effect of rhenium on the microstructure stability and γ/γ′ interfacial characteristics of Ni-based single crystal superalloys during long-term aging

Review of the hydrogen embrittlement and interactions between hydrogen and microstructural interfaces in metallic alloys: Grain boundary, twin boundary, and nano-precipitate

Unveiling the Re effect on long-term coarsening behaviors of γ′ precipitates in Ni-based single crystal superalloys

Atomistic investigation of hydrogen induced decohesion of Ni grain boundaries

Coupling between Re segregation and γ/γ′ interfacial dislocations during high-temperature, low-stress creep of a nickel-based single-crystal superalloy

Effect of alloy element on hydrogen-induced grain boundary embrittlement in BCC iron

Synergistic Effect of Rhenium and Ruthenium in Nickel-Based Single-Crystal Superalloys

Hydrogen-prompted heterogeneous development of dislocation structure in Ni

Study of Re strengthening mechanisms in nickel-based superalloy

Atomic-scale insights on hydrogen trapping and exclusion at incoherent interfaces of nanoprecipitates in martensitic steels

Enhanced Hydrogen Embrittlement Resistance via Cr Segregation in Nanocrystalline Fe–Cr Alloys

Grain boundary alloying segregation to resist hydrogen embrittlement in BCC-Fe steels: Atomistic insights into solute-hydrogen interactions