Abstract:Highly transparent, conductive nanosheets are extremely attractive for advanced opto-electronic applications. Previously, we have demonstrated that transparent, conductive Au nanosheets can be prepared by UV irradiation of Au nanoparticle (AuNP) monolayers spread on water, which serves as the subphase. However, thick Au nanosheets cannot be fabricated because the method is not applicable to large Au NPs. Further, in order to fabricate nanosheets with different thicknesses and compositions, it is necessary to prepare the appropriate NPs. A strategy is needed to produce nanosheets with different thicknesses and compositions from a single type of metal NP monolayer. In this study, we show that this UV irradiation technique can easily be extended as a nanosheet modification method by using subphases containing metal ions. UV irradiation of 4.7 nm AuNP monolayers on 480 μM HAuCl4 solution increased the thickness of Au nanosheets from 3.5 nm to 36.5 nm, which improved conductivity, but reduced transparency. On the other hand, the use of aqueous AgNO3 and CH3COOAg solutions yielded Au-Ag hybrid nanosheets; however, their morphologies depended on the electrolytes used. In Au-Ag nanosheets prepared on aqueous 500 μM AgNO3, Au and Ag metals are homogeneously distributed throughout the nanosheet. On the other hand, in Au-Ag nanosheets prepared on aqueous 500 μM CH3COOAg, AuNPs still remained and these AuNPs were covered with a Ag nanosheet. Further, these Au-Ag hybrid nanosheets had high conductivity without reduced transparency. Therefore, this UV irradiation method, modified by adding metal ions, is quite effective at improving and diversifying properties of Au nanosheets.

Galvanic replacement of mesh-like Ag nanosheets at an air-water interface

Conductive Nanosheets Fabricated from Au Nanoparticles on Aqueous Metal Solutions under UV Irradiation

Fabrication of flexible conductive nanosheets at air-water interface by UV irradiation of loosely-packed AgNPs monolayer

Conductive nanosheets produced by UV irradiation of a Ag nanoparticle monolayer at the air–water interface

Galvanic Replacement-Free Deposition of Au on Ag for Core-Shell Nanocubes with Enhanced Chemical Stability and SERS Activity.

Silver Nanowires Eelectrodeposited from Reverse Hexagonal Liquid Crystals

Water-phase synthesis of Au and Au–Ag nanowires and their SERS activity

Controllable synthesis of uncapped metal nanoparticle assembly at the air–water interface

Epitaxial growth of silver nanoislands on the surface of silicon nanowires in ambient air

Direct Synthesis of Au-Ag Nanoframes by Galvanic Replacement via a Continuous Concaving Process

Transformation of Ag Nanocubes into Ag-Au Hollow Nanostructures with Enriched Ag Contents to Improve Sers Activity and Chemical Stability

Direct Visualization of Laser-Induced Coalescence and Alloying of Au into Ag Nanowires

Au Nanoparticle Monolayer Nanosheets as Flexible Transparent Conductive Electrodes

Facile Synthesis Of Gold Wavy Nanowires And Investigation Of Their Growth Mechanism

Initiation and Progression of Anisotropic Galvanic Replacement Reactions in a Single Ag Nanowire: Implications for Nanostructure Synthesis

Hybrid Integration of Au Nanoplates and Ag Nanoparticles with Controlled Nanogaps via Cu2O‐mediated Galvanic Replacement Reaction: Plasmonic Catalysis and Photothermal Conversion

Ag Dendrite-Based Au/Ag Bimetallic Nanostructures with Strongly Enhanced Catalytic Activity.

Galvanic Replacement-Mediated Synthesis of Hollow Cu2O–Au Nanocomposites and Au Nanocages for Catalytic and SERS Applications

Single-crystalline Silver Nanowire Arrays Directly Synthesized Onto Substrates by Template-Assisted Chemical Wetting

Protecting the Nanoscale Properties of Ag Nanowires with a Solution-Grown SnO2 Monolayer As Corrosion Inhibitor

Surfactant-free synthesis of ultralong silver nanowires for durable transparent conducting electrodes