Robust Hybrid Omniphobic Surface for Stain Resistance
Zhengfeng Ma,Yang Wu,Rongnian Xu,Zhihuan Li,Yubo Liu,Jianxi Liu,Meirong Cai,Weifeng Bu,Feng Zhou
DOI: https://doi.org/10.1021/acsami.0c22834
2021-03-04
Abstract:Inspired by natural living surfaces, researchers have developed many excellent anti-smudge coatings, but there remain some critical challenges such as complex or expensive fabrications, poor long-term stability, non-transparency, etc., which may limit their large-area application. In this work, we designed a robust and transparent omniphobic coating with a one-step dip coating method. The perfluoropolyether chains were grafted on a smooth glass surface, and the coating surface not only presented good liquid repellency and stain resistance but also owned excellent mechanical wear resistance. The stain resistance property and wettability have barely changed after hundreds of thousands of friction cycles in air or even in an organic solvent surrounding. The robust hybrid coating possesses simple preparation, an excellent property, and durability, which may bring a widespread interest in the engineering application field.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c22834?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c22834</a>.The chemical equation of perfluoropolyether triethoxysilane (Figure S1), IR and TG of the hybrid coating compound (Figure S2), the AFM image of the raw glass surface (Figure S3), SEM of the hybrid omniphobic coating surface and cross profile (Figure S4), fine spectra of the C and O element before and after covering the hybrid coating (Figure S5), the summary of the contact angle and sliding angle of different liquids on the hybrid omniphobic coating (Table S1), the trace of the oily pen on the coating surface and raw glass surface (Figure S6), the photograph of the raw glass surface and the hybrid omniphobic coating surface after coating oily paint (Figure S7), the photograph of the omniphobic glass tube wetted by colza oil at different moments (Figure S8), appearance of the omniphobic pattern when dropping dyed toluene on the glass surface (Figure S9), the synthetic perspiration droplets on the hybrid coating (Figure S10), AFM and XPS of the hybrid coating after 200,000 friction cycles under 100 kPa (Figure S11), and the element content of the hybrid coating before and after 200,000 friction cycles under 100 kPa (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c22834/suppl_file/am0c22834_si_001.pdf">PDF</a>)Video of the water droplet dyed by methyl blue moving freely without any adhesive residue when sloping in the omniphobic tube (Movie S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c22834/suppl_file/am0c22834_si_002.mp4">MP4</a>)Video of the oil film gathering on the bottom of the tube without any adhesive residue on the inner wall (Movie S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c22834/suppl_file/am0c22834_si_003.mp4">MP4</a>)Video of the fast movement of the contact line of coating-ethanol-air that is noticeable at every friction cycle (Movie S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c22834/suppl_file/am0c22834_si_004.mp4">MP4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology