Abstract:Sulfide-modified nanoscale zerovalent iron (S-nZVI) has excellent reducing performance for heavy metals in water. The influence of environmental factors on the reactivity can be used to explore the practical feasibility of S-nZVI and analyze the reaction mechanism in depth. This study compared the removal effect and mechanism of Cu2+ and Ni2+ by nanoscale zerovalent iron (nZVI), S-nZVI, and carboxymethyl cellulose-modified nanoscale zerovalent iron (CMC-nZVI). The results show that the pseudo-first-order kinetic constant of Cu2+ removal by nZVI, S-nZVI, and CMC-nZVI was 1.384, 1.919, and 2.890 min−1, respectively, and the rate of Ni2+ removal was 0.304, 0.931, and 0.360 min−1, respectively. The removal mechanism of S-nZVI was similar to that of nZVI and CMC-nZVI. Specifically, Cu2+ was predominantly removed by reduction, while Ni2+ removal included adsorption and reduction. Environmental factors had a specific inhibitory effect on the removal of Cu2+ but had a negligible impact on Ni2+. The condition of low pH, the presence of Cl− and humic acid (HA) promoted the corrosion consumption of Fe0, in which H+ directly corroded Fe0 at low pH. At the same time, Cl− and HA inhibited the adsorption or binding of heavy metal ions on the particle surface, thereby reducing the electron transfer and utilization efficiency. The passivation of <math>NO3-</math> reduced the anaerobic corrosion of the material in water but suppressed the release of electrons, thereby reducing the reduction efficiency of the three types of materials. The anaerobic corrosion of S-nZVI was less affected by environmental factors, and it can still maintain more than 80% of the electronic utilization efficiency under different environmental factors, which illustrates that S-nZVI has broad prospects for practical applications in heavy metal polluted water.

Surface wettability control and electron transport regulation in zerovalent iron for enhanced removal of emerging polystyrene microplastics-heavy metal contaminants

Removal of micron-scale microplastic particles from different waters with efficient tool of surface-functionalized microbubbles

The feasibility and mechanism of poly-aluminum/titanium silicate composite coagulants for the efficient removal of nano- and micro-sized plastics

Attapulgite-supported sulfidated nano Zero-Valent Iron activated persulfate advanced oxidation technology for degradation of polyethylene microplastics: Optimal design, change of particle size and degradation mechanisms

Microplastics in Water: A Review of Characterization and Removal Methods

Nanoscale Zero-Valent Iron Dispersed by Sodium Alginate Enables Highly Efficient Removal of Lead (Pb) from Aqueous Solution

Ferrous ion enhanced Fenton-like degradation of emerging contaminants by sulfidated nanosized zero-valent iron with pH insensitivity

Enhanced Removal of Nanoplastics from Freshwater Using In-Situ Synthesized and Anchored Nano-Fe3o4 Via Two-Step Ferrous Oxidation

Enhanced removal performance of zero-valent iron towards heavy metal ions by assembling Fe-tannin coating

Effects of environmental factors on the removal of heavy metals by sulfide-modified nanoscale zerovalent iron

Enhanced adsorption and reduction of Pb(II) and Zn(II) from mining wastewater by carbon@nano-zero-valent iron (C@nZVI) derived from biosynthesis

Synthesis of carbon microsphere-supported nano-zero-valent iron sulfide for enhanced removal of Cr(VI) and p-nitrophenol complex contamination in peroxymonosulfate system

Interaction Between Pollutants During the Removal of Polychlorinated Biphenyl-Heavy Metal Combined Pollution by Modified Nanoscale Zero-Valent Iron

Nanoscale Zero-Valent Iron (nZVI) for Heavy Metal Wastewater Treatment: A Perspective

Efficient Removal of Nano- and Micro- Sized Plastics Using a Starch-Based Coagulant in Conjunction with Polysilicic Acid.

Optimizing Microplastic Removal Through Coagulation-Sedimentation with Permanganate Pre-oxidation and Pre-chlorination

Removal of heavy metals in water using nano zero-valent iron composites: A review

Enhanced Removal of Polystyrene Microplastics from Water Through Coagulation Using Polyaluminum Ferric Chloride with Coagulant Aids

Dual-supported nanoscale zero-valent iron for As(III) contaminated groundwater remediation

Removal of Polystyrene Microplastics from Aqueous Solution Using the Metal–Organic Framework Material of ZIF-67

Removal of microplastics from water by coagulation of cationic-modified starch: An environmentally friendly solution