Abstract:The oxygen reduction reaction (ORR) is a key “showstopper” for the commercial viability of alkaline fuel cells (AFCs). In this study, we developed a ternary nanocatalyst (NC) coloaded with Pt2Ni4 atomic clusters and palladium (Pd) nanoparticles (NPs) on oxygen vacancies (OVs) enriched nickel hydroxide-support (henceforth denoted as NiPP). This material outperforms the commercial J.M.-Pt/C (20 wt%) catalyst by ∼75 and ∼38 times with exceptionally high mass activities (MA)s of 5050.3 mAmgPt -1 and 952.3 mAmgPt -1 at 0.85 V and 0.90 V vs RHE, respectively, in alkaline ORR (0.1 M KOH). The high structural reliability of the Pt2Ni4 endows the NiPP NC with outstanding durability, where it achieves an optimum MA of 5755.9 mAmgPt -1 after 10 K cycles in an accelerated durability test (ADT) and retains the original performance up to 15 K cycles. Moreover, NiPP delivers an outstanding power density (339.1.4 mW cm−2) and short circuit current density (910.8 mA cm−2), which exceeds the commercial J.M.-Pt/C (174.9 mW cm−2 and 720.4 mA cm−2) when serving as the cathodic catalyst in an AFC. The results of physical characterizations, electrochemical analysis and in-situ XAS analysis suggest that the exceptional performance is originated from the potential synergism between the neighbouring reaction sites of Pt2Ni4 (OV in Ni(OH)x and Pd NPs). During ORR, the Pt2Ni4 atomic clusters and OVs boost the O2 splitting, while the adjacent Pd NPs promote the subsequent relocation of OH– ions. The obtained results provide the potential design strategies for the atomic-scale surface engineering of advanced ORR NCs in alkaline fuel cells.

Potential synergy between Pt2Ni4 Atomic-Clusters, oxygen vacancies and adjacent Pd nanoparticles outperforms commercial Pt nanocatalyst in alkaline fuel cells