Tip‐Enhanced Electric Field: A New Mechanism Promoting Mass Transfer in Oxygen Evolution Reactions

Peng Liu,Bo Chen,Caiwu Liang,Wentao Yao,Yuanzheng Cui,Shengyu Hu,Peichao Zou,Hua Zhang,Hong Jin Fan,Cheng Yang
DOI: https://doi.org/10.1002/adma.202007377
IF: 29.4
2021-01-29
Advanced Materials
Abstract:<p>The slow kinetics of oxygen evolution reaction (OER) causes high power consumption for electrochemical water splitting. Various strategies have been attempted to accelerate the OER rate, but there are few studies on regulating the transport of reactants especially under large current densities when the mass transfer factor dominates the evolution reactions. Herein, Ni<i><sub>x</sub></i>Fe<sub>1–</sub><i><sub>x</sub></i> alloy nanocones arrays (with ≈2 nm surface NiO/NiFe(OH)<sub>2</sub> layer) are adopted to boost the transport of reactants. Finite element analysis suggests that the high‐curvature tips can enhance the local electric field, which induces an order of magnitude higher concentration of hydroxide ions (OH<sup>−</sup>) at the active sites and promotes intrinsic OER activity by 67% at 1.5 V. Experimental results show that a fabricated NiFe nanocone array electrode, with optimized alloy composition, has a small overpotential of 190 mV at 10 mA cm<sup>−2</sup> and 255 mV at 500 mA cm<sup>−2</sup>. When calibrated by electrochemical surface area, the nanocones electrode outperforms the state‐of‐the‐art OER electrocatalysts. The positive effect of the tip‐enhanced local electric field in promoting mass transfer is also confirmed by comparing samples with different tip curvature radii. It is suggested that this local field enhanced OER kinetics is a generic effect to other OER catalysts.</p>
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology
What problem does this paper attempt to address?
The paper primarily focuses on addressing the slow kinetics of the oxygen evolution reaction (OER) during alkaline water electrolysis, which is a critical bottleneck affecting the overall efficiency of water electrolysis. Specifically, the research team in the paper designed and prepared a novel NiFe nanocone array catalyst, aiming to enhance the local electric field to promote the mass transfer of reactants, thereby improving the catalytic activity of OER. To achieve this goal, the researchers employed high-curvature NiFe nanocone arrays as the catalyst. Through finite element analysis (FEA) simulations and experimental validation, they found that the tips of these nanocones could enhance the local electric field strength, significantly increasing the concentration of hydroxide ions (OH⁻) near the active sites. This not only reduced the overpotential of OER but also improved the catalytic performance at high current densities. Specific achievements include: 1. The NiFe nanocone array exhibited excellent OER performance under optimized alloy composition, with an overpotential of only 190 mV at 10 mA cm⁻² and 255 mV at 500 mA cm⁻². 2. Compared to state-of-the-art OER catalysts, the nanocone array showed higher catalytic activity after electrochemical surface area correction. 3. By altering the curvature radius of the nanocone tips, the importance of local electric field enhancement in improving OER activity was further demonstrated. 4. Long-term stability tests indicated that the catalyst maintained excellent stability and durability even at high current densities up to 1000 mA cm⁻². In summary, this study proposes a novel mechanism—enhancing mass transfer through local electric field enhancement, effectively improving the kinetics of OER, which is of great significance for enhancing the overall efficiency of alkaline water electrolysis.