Heterojunction of Vertically Arrayed MoS 2 Nanosheet/N-Doped Reduced Graphene Oxide Enabling a Nanozyme for Sensitive Biomolecule Monitoring
Longwei Wang,Bo Li,Zhen You,Aizhu Wang,Xuanyu Chen,Gaojing Song,Ling Yang,Dan Chen,Xin Yu,Jing Liu,Chunying Chen
DOI: https://doi.org/10.1021/acs.analchem.1c01550
IF: 7.4
2021-08-03
Analytical Chemistry
Abstract:Enzymes are still indispensable for bio-assaying methods in biomolecule detection by far. The unsatisfied long-term instability, high cost, and susceptibility to the physical environment of natural enzymes are obvious weak points. Here, we developed peroxidase-like heterostructured nanozyme, vertically arraying molybdenum disulfide nanosheets on a substrate layer of nitrogen-doped reduced graphene oxide (MoS2/N-rGO), with a well-pleasing stability that is characterized by the retained enzymatic activity and maintained structure after 2 years of casual storage at ambient temperatures or 80 cycles of catalytic reaction. The catalytic kinetics of the as-prepared heterostructured nanozyme was superior to some reported nanozymes and even horse radish peroxidase, which was demonstrated due to the defect-rich MoS2 with Mo and S vacancies and nitrogen-doped rGO experimentally and theoretically. The vertically heterostructured nanozyme exhibited adequate analytical performance in sensitive and quantitative detection of glucose and glutathione (GSH), with a large dynamic sensing range and extremely low limit of detection (0.02 and 0.12 μM (3σ/slope) for glucose and GSH, respectively). We hope this inspired artificial nanozyme will contribute to the future development in sensitive detection of other biomolecules in physiological conditions.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.analchem.1c01550.Schematic of MoS2 models, charge density difference of perfect MoS2 surfaces, charge density different of MoS2 with Vs surfaces, charge density different of MoS2 with VMo+ VS surfaces, charge density different of N-rGO surfaces, intermediates during the H2O2 decomposition process on the rGO surface without (a) and with (b) N doping, schematic illustration and charge density different of rGO lattice with 2OH* adsorption and OH* adsorption, schematic illustration and charge density difference of N-rGO lattice with 2OH* adsorption and OH* adsorption, schematic illustration and charge density difference of rGO lattice with O* + OH* adsorption and O* adsorption, schematic illustration and charge density difference of N-rGO lattice with O* + OH* adsorption and O* adsorption, SEM images of microwave-assisted hydrothermal synthesized pure rGO, Scanning SEM and EDS elemental maps of C, N and overlay of N-rGO, SEM mage and EDS elemental maps of C, S, Mo and overlay of the MoS2/rGO vertical heterostructure, SEM images of microwave-assisted hydrothermal synthesized pure M-MoS2, SEM images of the microwave-assisted hydrothermal synthesized MoS2 /N-rGO-5 heterostructure, SEM images of the oven hydrothermal synthesized MoS2 /N-rGO heterostructure, Raman spectra of the MoS2/N-rGO vertical heterostructure, XPS spectra of the MoS2/N-rGO vertical heterostructure, high-resolution XPS spectra of C 1s for the MoS2/N-rGO vertical heterostructure, Nyquist plots of the different samples, time-dependent absorbance changes at 652 nm of POD-like activity for the rGO and N-rGO, the MoS2/rGO and MoS2/N-rGO, catalytic activity of the different samples after 80 catalytic reaction cycles, absorbance at 652 nm of POD-like activity after 5 minutes, SEM images of MoS2 /N-rGO after 2 years of casual storage, and UV–vis absorption curves of MoS2/N-rGO with TMB and H2O2in the presence of different concentrations of GSH at pH 3.6 (PDF)This article has not yet been cited by other publications.
chemistry, analytical