A spherical TiO2-Bi2WO6 composite photocatalyst for visible-light photocatalytic degradation of ethylene

Rui Wang,Mei Xu,Jiawen Xie,Shengying Ye,Xianliang Song

DOI: https://doi.org/10.1016/j.colsurfa.2020.125048

2020-10-01

Abstract:In this paper, Bi2WO6 porous microspheres were prepared via a hydrothermal method and nano-TiO2 uniformly dotted on the surface of the Bi2WO6 microspheres using deposition technology to self-assemble a porous layer spherical TiO2-Bi2WO6 (TB) composite photocatalyst. The photocatalytic activity of the composite photocatalyst was evaluated using ethylene as the target degradation product. The results show that the photocatalytic degradation of ethylene by the TB composite photocatalyst was significantly improved, especially 10 % TB. Samples containing 10 % titanium dioxide had the highest photocatalytic activity for ethylene degradation. In addition, the degradation rate of ethylene was as high as 20.90 %, which was 1.53 times higher than that of Bi2WO6 microspheres. The spherical structure of the porous layer gives the composite photocatalyst a high specific surface area, which can effectively promote the rapid migration of photogenerated carriers between TiO2 and Bi2WO6, and prevent the recombination of photogenerated electrons and photogenerated holes, thereby effectively improving the photocatalytic performance.

chemistry, physical

What problem does this paper attempt to address?

The main problem this paper attempts to address is the development of an efficient visible-light-responsive photocatalyst for the degradation of ethylene. Specifically, the authors self-assembled a three-dimensional porous spherical TiO₂-Bi₂WO₆ composite photocatalyst (TB) through hydrothermal and deposition techniques, aiming to enhance its photocatalytic activity under visible light, particularly in the application of ethylene degradation. The study found that when the TiO₂ content was 10%, the composite photocatalyst exhibited the best photocatalytic performance, with an ethylene degradation rate of up to 20.90%, which is 1.53 times higher than that of pure Bi₂WO₆ microspheres. This composite structure not only increased the specific surface area of the photocatalyst but also effectively promoted the rapid migration of photogenerated carriers between TiO₂ and Bi₂WO₆, reducing the recombination of photogenerated electrons and holes, thereby significantly improving the photocatalytic performance.