Realizing the invariant electrostrain response and low hysteresis via multicomponent coordination in Pb‐based ceramics
Zhen Li,Hongrui Jia,Jintao Lu,Yinfei Li,Zhigang Liang,Jing Wei,Linghang Wang
DOI: https://doi.org/10.1111/jace.19107
IF: 4.186
2023-04-06
Journal of the American Ceramic Society
Abstract:High‐performance piezoelectric materials are essential in many piezoelectric devices. However, the composition of piezoelectric materials usually has a great influence on their performance. In this work, xBi(Mg1/2Ti1/2)O3‐yPbZrO3‐zPbTiO3 (xBMT‐yPZ‐zPT; 0.2≤x≤0.4, 0.25≤y≤0.4, and 0.35≤z≤0.4.) ternary ceramics with different compositions were synthesized and the strain response was not sensitive to the composition was found at the same time. The crystal structure, strain response, ferroelectric properties, and the temperature stability of xBMT‐yPZ‐zPT ceramics were investigated in details. X‐ray diffraction patterns show all the as‐prepared xBMT‐yPZ‐zPT ceramics with x = 0.2, 0.3, 0.4 and 0.5 possess a perovskite structure. Under the external electric field of 6 kV mm−1, the strain value of xBMT‐yPZ‐zPT ternary ceramics with x = 0.2, 0.3, 0.4, and 0.5 was 0.30 %, 0.31%, 0.30 % and 0.27 %, respectively. In addition, the strain hysteresis of these ternary ceramics is also almost the same and low. These merits make xBMT‐yPZ‐zPT piezoelectric ceramics have broad application prospect in the field of commercial actuators. This article is protected by copyright. All rights reserved
materials science, ceramics