A Kinetic Study on Crystallization in TiO2-SiO2-CaO-Al2O3 Glass under Nucleation Saturation Conditions for the High Value-Added Utilization of CaO-SiO2-Based Solid Wastes

Zhen Wang,Renze Xu
DOI: https://doi.org/10.3390/ma16114165
IF: 3.4
2023-06-03
Materials
Abstract:A kinetic study of the non-isothermal crystallization of CaO-SiO2-Al2O3-TiO2 glass was carried out using the Matusita–Sakka equation and differential thermal analysis. As starting materials, fine-particle glass samples (<58 μm), case defined as ''nucleation saturation'' (i.e., containing such a large number of nuclei that the nucleus number is invariable during the DTA process), became dense bulk glass–ceramics through heat treatment, demonstrating the strong heterogeneous nucleation phenomenon at the juncture of particle boundaries under "nucleation saturation" conditions. Three types of crystal phase are formed during the heat treatment process: CaSiO3, Ca3TiSi2(AlSiTi)3O14, and CaTiO3. As the TiO2 content increases, the main crystal shifts from CaSiO3 to Ca3TiSi2(AlSiTi)3O14. The EG values (activation energy of crystal growth) are in the 286–789 kJ/mol range. With increasing TiO2, EG initially decreases (the minimum appears at 14% TiO2), and then, increases. When added within 14%, TiO2 is shown to be an efficient nucleating agent that promotes the growth of wollastonite in a two-dimensional mechanism. As TiO2 further increases to exceed 18%, it is no longer just a nucleating agent but becomes one of the major components in the studied glass, so, in turn, it undermines the crystallization of wollastonite by forming Ti-bearing compounds, resulting in a tendency toward surface crystallization and higher activation energy of crystal growth. For glass samples with fine particles, it is important to note the "nucleation saturation" case for a better understanding of the crystallization process.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: to study the influence of titanium dioxide (TiO₂) on the crystal growth mechanism and crystallization activation energy in the non - isothermal crystallization process of calcium - silicon - aluminum - titanium glass (CaO - SiO₂ - Al₂O₃ - TiO₂ glass) under the "nucleation saturation" condition, so as to promote the high - value utilization of metallurgical slag and the development of high - performance ceramics. Specifically, the paper focuses on the following aspects: 1. **Crystal growth mechanism**: By studying the non - isothermal crystallization behavior of CaO - SiO₂ - Al₂O₃ - TiO₂ glass with different TiO₂ contents under the "nucleation saturation" condition, the change of the crystal growth mechanism is explored. 2. **Crystallization activation energy**: Calculate the crystallization activation energy (\(E_G\)) of the glass with different TiO₂ contents and analyze its variation law. 3. **Crystal phase formation**: Determine the crystal phases formed with different TiO₂ contents and analyze the relative content changes of these crystal phases. ### Main research contents - **Sample preparation**: Glass samples with different TiO₂ contents were prepared by the melting - quenching method. - **Differential thermal analysis (DTA)**: DTA tests were carried out on glass samples at different heating rates to obtain the thermal effect data during the crystallization process. - **Crystal identification and phase analysis**: Crystal phase and morphology analysis were carried out on the crystallized samples by X - ray diffraction (XRD) and scanning electron microscopy (SEM) combined with energy - dispersive spectroscopy (EDS). - **Crystallization kinetic analysis**: Kinetic analysis of the non - isothermal crystallization process was carried out using the Matusita - Sakka equation to calculate the crystallization activation energy and the crystal growth mechanism. ### Research significance - **Waste utilization**: By studying the crystallization characteristics of the CaO - SiO₂ - Al₂O₃ system in metallurgical slag, it provides a scientific basis for the high - value utilization of metallurgical slag. - **Material development**: A deep understanding of the influence of TiO₂ on the crystallization behavior of CaO - SiO₂ - Al₂O₃ glass is helpful for the development of glass - ceramic materials with excellent properties. ### Conclusions - **Crystal phase change**: With the increase of TiO₂ content, the main crystal changes from CaSiO₃ to Ca₃TiSi₂(AlSiTi)₃O₁₄. - **Crystallization activation energy**: When the TiO₂ content is below 14%, the crystallization activation energy first decreases and then increases; when the TiO₂ content exceeds 18%, Ti - containing compounds are formed, resulting in surface crystallization and a relatively high crystallization activation energy. - **Crystal growth mechanism**: In the range of 10% - 18% TiO₂ content, the crystal growth is mainly a two - dimensional mechanism; when the TiO₂ content is 22%, surface crystallization and one - dimensional growth mechanism appear. Through these studies, the paper provides an important scientific basis for understanding the crystallization behavior of CaO - SiO₂ - Al₂O₃ - TiO₂ glass, which is helpful to promote the application and development in related fields.