Abstract:Excellent electromagnetic wave (EMW) absorbing materials with high-temperature stable and superior mechanical properties are among the most promising candidates for practical application. Here, novel hydrothermal carbon coated three-dimensional (3D) needled carbon fiber reinforced silicon-boron carbonitride (HC-CF/SiBCN) composites with a hierarchical A (CF)/B (HC)/C (SiBCN) structure were constructed and prepared for the first time by combining hydrothermal transformation and precursor infiltration and pyrolysis (PIP) process. The thickness of the HC coating controlled by the glucose concentration played a crucial role in tailoring the EMW capacity of the composite. The incorporation of SiBCN could not only effectively improve the oxidation resistance but also actively enhance the mechanical properties of the HC coated CF structure. Compared to the weak high-temperature oxidation resistance and mechanical properties of pristine 3D needled CF felt, the composites after the introduction of HC and SiBCN were thermostable in air atmosphere beyond 1000 degrees C to about above 70% weight retention, and the maximum flexural and compression strength of the composites could reach to 23.51 +/- 1.37 and 12.22 +/- 1.12 MPa, respectively. A substantial enhancement of EMW absorption ability was achieved through incorporation of HC and SiBCN, which could be attributed to the matched characteristic impedance and enhanced loss ability, whose optimization EMW absorption performance was the minimum reflection loss (RLmin) of-52.08 dB and effective absorption bandwidth (EAB) of 7.64 GHz for the composite obtained by two PIP cycles with 24 wt% glucose solution, demonstrating that the HC-CF/SiBCN composites with high-temperature stable, excellent mechanical and superior EMW absorption properties could be considered as a promising candidate for the applications in harsh environments. (C) 2020 Elsevier Inc. All rights reserved.

Multimaterial 3D-printing barium titanate/carbonyl iron composites with bilayer-gradient honeycomb structure for adjustable broadband microwave absorption

Multimaterial 3D-printing of graphene/Li0.35Zn0.3Fe2.35O4 and graphene/carbonyl iron composites with superior microwave absorption properties and adjustable bandwidth

Designing Symmetric Gradient Honeycomb Structures with Carbon-Coated Iron-Based Composites for High-Efficiency Microwave Absorption

Design on the Microwave Absorber with Lattice of 3D Composite Element for X-band Application

Millimeter-wave absorption properties of BaTiO3/Co3O4 composite powders controlled by high-frequency resonances of permittivity and permeability

3D Printed Labyrinth Multiresonant Composite Metastructure for Broadband and Strong Microwave Absorption

Dual gradient direct ink writing of functional geopolymer-based carbonyl-iron/graphene composites for adjustable broadband microwave absorption

A wide-angle broadband electromagnetic absorbing metastructure using 3D printing technology

Layered-structure N-doped Expanded-Graphite/boron Nitride Composites Towards High Performance of Microwave Absorption

Bamboo-inspired Composite Metastructure for Broadband Microwave Absorption and Load Bearing

Multi-material fused deposition modelling of structural–functional integrated absorber with multi-scale structure possessing tunable broadband microwave absorption

Strong and Thermostable Hydrothermal Carbon Coated 3D Needled Carbon Fiber Reinforced Silicon-Boron Carbonitride Composites with Broadband and Tunable High-Performance Microwave Absorption.

Metastructure based broadband structural stealth with material-structure-function integration

3D-printed carbon fiber/polyamide-based flexible honeycomb structural absorber for multifunctional broadband microwave absorption

2D/2D coupled MOF/Fe composite metamaterials enable robust ultra-broadband microwave absorption

Multi-scale structural design of multilayer magnetic composite materials for ultra-wideband microwave absorption

Microwave absorption performance of sandwich-like Ti3C2Tx@BFO composite material in C and X bands

Integrated lightweight gradient honeycomb metastructure with microwave absorption and mechanical properties: analysis, design, and verification

Multi-Scale Integrated Design And Fabrication Of Ultrathin Broadband Microwave Absorption Utilizing Carbon Fiber/Prussian Blue/Fe3o4-Based Lossy Lattice Metamaterial

3D Printed Carbon Based All-dielectric Honeycomb Metastructure for Thin and Broadband Electromagnetic Absorption

Ultra-Thin and Broadband P-Band Metamaterial Absorber Based on Carbonyl Iron Powder Composites