Rapid in situ hepatic hemostasis using a P34HB/tranexamic acid fibrous membrane delivered by a handheld electrospinning apparatus

Shunen Xu,Long Yang,Xin Wu,Yong Yang,Yuhu Zhou,Chuan Ye

DOI: https://doi.org/10.1007/s10965-022-03174-4

IF: 3.061

2022-07-10

Journal of Polymer Research

Abstract:In the current study, fibrous membrane based on poly(3-hydroxybutyrate- co-4-hydroxybutyrate) (P34HB) and tranexamic acid (TA) were manufactured by a handheld electrospinning apparatus for the first time. Electrospun fibers were fabricated using 6% P34HB with different concentrations of TA particles(10, 20, and 30 wt%). The structure of the fiber was observed under an electron microscope, and the properties of the material were examined by X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. The release rate of TA was measured, and Alamar Blue staining and Live/dead staining were used to detect cell proliferation and biocompatibility. Animal experiments were done to verify the hemostatic effect on the liver. SEM showed that the electrospun fiber had a micro-/nanostructure with a diameter of 100 nm to 3 μm. XRD and FTIR showed that P34HB and TA were not chemically cross-linked in the fiber membrane. As the TA concentration increased, the hydrophilicity of the fiber increased, and the release rate of TA was 50% at 30 s, 70% at 30 min, and approximately 90% at 1 h. Alamar Blue staining and Live/dead staining confirmed that P-20%TA had low cytotoxicity to human endothelial cells and rat hepatocytes, in vivo experiments confirmed that P-20%TA achieved rapid hemostasis of the liver within 10–20 s, HE staining indicated that P34HB was partially degraded in the body by 1 week, and neovascular tissue formation was observed in the wound. Therefore, our results can be employed for biomaterials aimed at immediately stop bleeding and promote the repair of liver wound.

polymer science