A High-Efficient Carbon-Coated Iron-Based Fenton-Like Catalyst with Enhanced Cycle Stability and Regenerative Performance

Xin Li,Jiankang Wang,Xiao Zhang,Xianjin Hou,Hongbo Xu,Zhongping Yao,Zhaohua Jiang

DOI: https://doi.org/10.3390/catal10121486

IF: 3.9

2020-12-19

Catalysts

Abstract:Carbon coated iron-based Fenton-like catalysts are now widely studied in wastewater treatment. However, their poor stability is still a big challenge and the related regenerative performance is seldom investigated. Herein, a carbon-coated Fe3O4 on carbon cloth (cc/Fe3O4@C) was prepared with glucose as carbon source via electrodeposition and ethanol solvothermal methods. An amorphous carbon layer with polar C-groups covers the surface of Fe3O4, which presents a flaky cross-linked network structure on the carbon cloth (cc). The cc/Fe3O4@C exhibits an improved catalytic activity with nearly 84% phenol was removed within 35 min with polar C-groups. What’s more, around 80% phenol can still be degraded in 120 min after 14 degradation cycles. After the regeneration treatment, the degradation performance was restored to the level of the fresh in the first two regenerations. The enhanced cycle stability and regeneration performance of the catalyst are as follows: Firstly, the catalyst’s composition and structure were recovered; Secondly, the reduction effect of the amorphous carbon layer ensuring timely supplement of Fe2+ from Fe3+. Also, the carbon layer reduces Fe leaching during the Fenton-like process.

chemistry, physical

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the insufficient stability and regeneration performance of iron - based Fenton - like catalysts in wastewater treatment applications. Specifically:

1. **Stability problem**: Traditional iron - based Fenton - like catalysts (such as Fe₂O₃) are prone to problems of decreased activity and iron dissolution during the recycling process, resulting in a gradual weakening of the catalytic performance.
2. **Regeneration performance problem**: At present, there are relatively few studies on the regeneration performance of iron - based Fenton - like catalysts, and there is a lack of effective regeneration methods to restore their catalytic activity.

To solve these problems, the author developed a carbon - coated Fe₃O₄ catalyst (cc/Fe₃O₄@C), which was synthesized by electrodeposition and ethanol - solvothermal method, with glucose as the carbon source. This catalyst has the following advantages:

- **Enhanced cycle stability**: The carbon layer can reduce iron dissolution and maintain the structural integrity of the catalyst, thereby improving its stability during recycling.
- **Excellent regeneration performance**: After regeneration treatment by the ethanol - solvothermal method, the catalyst can be restored to a catalytic activity close to the initial one, showing good regeneration performance.

Therefore, this research aims to improve the stability and reusability of iron - based Fenton - like catalysts in practical applications, especially in the field of wastewater treatment, by improving the structure of the catalyst and the regeneration method.