Abstract:Hard carbon (HC) stands out as the preeminent anode material for sodium-ion batteries (SIBs) which are deployed in expansive energy storage infrastructures. Herein, the large enough graphene nanosheets interlayer and abundant nanopores with a diameter of ∼2.1 nm induced by adjusting the pyrolysis temperature in the thermosetting phenolic resin-derived hard carbon matrix to augment the performance of the sodium ion storage. The presence of sufficiently large carbon interlayers has been proven to provide active sites for reversible adsorption, enabling effective storage of sodium ions in the high-voltage slope region, while also promoting rapid Na + transport. Meanwhile, forming abundant closed nanopores with larger sizes helps sodium ion storage in the low-voltage plateau region. In the optimized samples, the formation of sufficient long graphene nanosheets with a perfect crystal lattice, which further shrinks to form enclosed nanopores, effectively reduces defective sites and specific surface area. Additionally, the appropriate content of C-O and C=O functional groups contributes to an exceptional initial Coulombic efficiency (ICE) of up to 93%. Simultaneously, the optimized sample HC-1500 contributes to a remarkable plateau capacity of 294 mAh g - 1 during the charging process (high reversible capacity of 403 mAh g - 1 at 0.1 C). Moreover, based on the microstructure evolution and Na storage behavior of hard carbon, an "adsorption (27%) – filling (73%)" sodium storage mechanism that the sodium storage as a quasi-metallic sodium state is demonstrated. Consequently, this study will offer valuable insights for the development of hard carbon anodes tailored for high-energy practical SIBs, while also advancing the understanding of sodium storage mechanisms.

Hard Carbon Microtubes Made from Renewable Cotton as High‐Performance Anode Material for Sodium‐Ion Batteries

Revitalizing Sodium-Ion Batteries Via Controllable Microstructures and Advanced Electrolytes for Hard Carbon

Biomass-derived hard carbon microtubes with tunable apertures for high-performance sodium-ion batteries

Low Temperature Carbonization of Cellulose Nanocrystals for High Performance Carbon Anode of Sodium-Ion Batteries

Sodium‐Ion Batteries: Hard–Soft Carbon Composite Anodes with Synergistic Sodium Storage Performance (adv. Funct. Mater. 24/2019)

A Life Cycle Assessment of Hard Carbon Anodes for Sodium-Ion Batteries

Hard Carbon/graphene Microfibers As a Superior Anode Material for Sodium-Ion Batteries

Hard Carbon Microsphere with Built-In Electron Transport Channels as a High-Performance Anode for Sodium-Ion Batteries

From Natural Fibers to High-Performance Anodes: Sisal Hemp Derived Hard Carbon for Na-/K-Ion Batteries and Mechanism Exploration

High temperature induced abundant closed nanopores for hard carbon as high-performance sodium-ion batteries anodes

Hard Carbon Microsphere with Expanded Graphitic Interlayers Derived from a Highly Branched Polymer Network as Ultrahigh Performance Anode for Practical Sodium-Ion Batteries

From Micropores to Ultra-micropores inside Hard Carbon: Toward Enhanced Capacity in Room-/Low-Temperature Sodium-Ion Storage

Sulfur-doping biomass based hard carbon as high performance anode material for sodium-ion batteries

Boosting the Initial Coulomb Efficiency of Sisal Fiber-Derived Carbon Anode for Sodium Ion Batteries by Microstructure Controlling

Development of Biomass‐Derived Hard Carbon for Sodium‐Ion Batteries: Optimizing Microstructure and Electrochemical Performance

Industrial‐scale Hard Carbon Designed to Regulate Electrochemical Polarization for Fast Sodium Storage

Sustainable Fabrication of a Practical Hard Carbon Anode for a Sodium-Ion Battery with Unprecedented Long Cycle Life

Hard carbon derived from waste tea biomass as high-performance anode material for sodium-ion batteries

Low-Cost and High-Performance Hard Carbon Anode Materials for Sodium-Ion Batteries

Interlaced Micro-Fibrous Hard Carbon As Superior Anode for Na-Ion Battery: Insights into the Sodium Storage Mechanism and Solid Electrolyte Interface

Electrochemical Characterization of Charge Storage at Anodes for Sodium‐Ion Batteries Based on Corncob Waste‐Derived Hard Carbon and Binder