Resource-recycling and energy-saving innovation for iron removal in hydrometallurgy: Crystal transformation of ferric hydroxide precipitates by hydrothermal treatment

Zhen Niu,Gaibian Li,Dongdong He,Xinzhuang Fu,Wei Sun,Tong Yue

DOI: https://doi.org/10.1016/j.jhazmat.2021.125972

IF: 13.6

2021-08-01

Journal of Hazardous Materials

Abstract:<p>In hydrometallurgy industry, the accumulation of iron removal residues containing heavy metal elements and toxic elements poses great threats to ecological systems. We propose a novel method to prevent the production of hazardous iron removal residues: firstly, neutralization precipitation is used to purify iron ions in solution; after sedimentation of the obtained suspension, only dense underflow is subjected to hydrothermal reaction, in which ferric hydroxide transforms into hematite crystal. Results showed that ferric hydroxide precipitated into a thin sedimentation layer at temperature greater than 60 °C. For hydrothermal treatment of the sedimentation layer, a high hydrothermal reaction temperature was conducive to complete transformation of ferric hydroxide into hematite. The precipitated ferric hydroxide firstly changed from the crystallite of goethite or lepidocrocite to amorphous particles, and then gradually formed spherical α-Fe₂O₃ monocrystalline with diameter of around 50 nm, as indicated by TEM and XRD results. At 200 °C, hematite precipitates with iron content of about 65% can be obtained. For iron-containing zinc/nickel/cobalt sulfate solution, controlling hydrothermal reaction temperature and acidity of the underflow solution can effectively avoid the generation of zinc/nickel/cobalt hydroxides or subsulfates in the hematite precipitates, thereby significantly reducing the loss of those valuable metals.</p>

environmental sciences,engineering, environmental

What problem does this paper attempt to address?

The paper aims to address the environmental and resource recovery issues caused by iron removal residues in the hydrometallurgical process. Specifically, the paper proposes an innovative method to achieve efficient iron removal and conversion through two stages:

1. **Neutralization Precipitation**: First, neutralization and precipitation of iron ions are carried out in the solution.
2. **Hydrothermal Conversion**: The obtained precipitate is subjected to hydrothermal treatment to convert ferric hydroxide into hematite, thereby achieving the recycling of iron resources.

This method not only reduces the generation of harmful iron removal residues but also significantly lowers energy consumption and increases iron content, making the final product reusable as raw materials for iron ore, cement, or pigments. Additionally, this method effectively prevents the loss of valuable metals such as zinc, nickel, and cobalt during the treatment process, reducing resource waste and economic loss. Through experimental studies under different conditions, the paper systematically optimizes the sedimentation performance and crystal conversion process of iron precipitates and verifies its feasibility in practical applications.