Abstract:In this paper, initiation and growth behavior tests of small fatigue crack in laboratory air and aqueous 3.5% NaCl were conducted using non-corroded and pre-corroded SENT specimens for 2024-T62 Aluminum alloy. In order to compare with the corresponding small cracks, large crack growth tests for non-corroded and corroded specimens with different prior corrosion times were performed. Variation of pre-corrosive pit sizes with corrosion time was also studied. The results show that for fatigue specimens with pre-corrosive pits, small cracks initiated from the corrosion pits in both laboratory air and aqueous 3.5% NaCl, and initiation lives of small cracks (a≤60μm) are below 25% of total fatigue lives. For non-corroded fatigue specimens in laboratory air, small cracks initiated naturally from voids of the material, and initiation lives of small cracks (a≤25μm) are below 20% of total fatigue lives. An obvious small crack effect was found at R=-1 for non-corroded material in laboratory air. However, the same effect was not found at R=0.06 for the non-corroded material in laboratory air, and for the corroded material in both laboratory air and aqueous 3.5% NaCl at R=-1 and 0.06. And effect of environment on growth of small cracks that initiated from pre-corrosive pits was not found for Al2024-T62. The similar tendency was also found in large crack growth tests. Moreover, effect of prior corrosion time on large crack growth rates was not found to be in existence for this material. By assuming a pre-corrosive pit as an initiating surface crack, the commercial software FASTRANII and AFGROW were used to predict fatigue lives of corroded specimens with different prior corrosions. The predictions were found to agree reasonably with the tests.

Influence of Pre-stress Corrosion on Fatigue Life of 2A12-T4 Aluminum Alloy

A study on the mean stress relaxation behavior of 2124-T851 aluminum alloy during low-cycle fatigue at different strain ratios

Investigation on corrosion fatigue properties of TA15 alloy in 3.5%NaCl salt spray

Strain Ratio Effects on Low-Cycle Fatigue Behavior and Deformation Microstructure of 2124-T851 Aluminum Alloy

Multiaxial Fatigue of 6061-T6 Aluminum Alloy under Corrosive Environment

Environment-induced Fatigue Cracking Behavior of Aluminum Alloys and Modification Methods

Influence of Water in Fuel Tank Environments on Fatigue Property of Precorroded Aluminum Alloy

Fatigue Life Evolution of Steel Wire Considering Corrosion-Fatigue Coupling Effect: Analytical Model and Application

INFLUENCE OF STRESS AMPLITUDE AND CORROSIVE FACTORS ON CORROSION FATIGUE LIFE OF RIVETED JOINTS

Effect of Prior Corrosion State on the Fatigue Small Cracking Behaviour of 6151-T6 Aluminum Alloy

A Study on the Corrosion Fatigue Characteristics of Al 2024-T3 Alloy

Influence of Saline Environment on Fatigue Property of Pre-Corroded Aluminum Alloy

Study on the Correlation between the Microstructure Characteristics and Corrosion Behaviors of 2A12-T4 Aluminum Alloy under Thermal Strain

Small fatigue crack behavior and life prediction of pre-corroded 2024-T62 aluminum alloy

The Effects of Corrosive Media on Fatigue Performance of Structural Aluminum Alloys

Influence of mean stress and overaging on fatigue life of aluminum alloy EN AW-2618A

STUDY OF CORROSION FATIGUE FOR LY12CZ ALUMINUM ALLOY RIVETED LAP-SPLICE JOINTS

Synergistic Effect of Environmental Media and Stress on the Fatigue Fracture Behaviour of Aluminium Alloys

In situ corrosion fatigue life of 2198-T8 Al–Li alloy based on tests and DIC technique

Effects of Stress Ratios on Aero High-strength LD2CZ Aluminum Alloy Fatigue Crack Growth with Corrosion Damage

Fatigue Corrosion Behavour of 2024-T3 Aluminum Alloy with 4 Surface Protective Coatings