Theoretical and experimental insights of two surfactants' effects on SnIn electrodeposited coatings from ethaline
José Osmar de Souza,Natalia Gomes Sousa,Renato Veríssimo de Oliveira,Lucas Lima Bezerra,Paulo Naftali da Silva Casciano,Adriana Nunes Correia,Pedro de Lima Neto,Norberto de Kássio Vieira Monteiro
DOI: https://doi.org/10.1016/j.molstruc.2024.140668
IF: 3.841
2024-11-22
Journal of Molecular Structure
Abstract:This work uses computational methodologies to investigate the behavior of Sn 2+ and In 3+ ions in deep eutectic solvent (DES) based on choline chloride and ethylene glycol (1ChCl:2EG, ethaline), under different conditions, such as different temperatures, ion ratios, and in the presence and absence of hexadecyltrimethylammonium bromide (CTAB) and sodium dodecyl sulfate (SDS) surfactants. Furthermore, SnIn alloys were electrodeposited on Cu surfaces to analyze the effect of the investigated different conditions on the surface morphology and chemical composition of the electrodeposited coatings. Morphology and composition were analyzed using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray (EDS). For computational approach, twelve Molecular Dynamics (MD) simulations were conducted using the GROMACS software. After MD simulations, Quantum Theory of Atoms in Molecules (QTAIM) properties were obtained. The results presented that In 3+ showed a stronger affinity for Cl − than Sn 2+ but it presents weaker and less stable interactions with OA (OA = oxygen of ethylene glycol-EG), particularly at higher temperatures. Electron Density and Electron Localization Function analysis indicated that In-Cl interactions are stronger and more polarized than other interactions. The Laplacian of Electron Density suggested an intermolecular nature for all interactions. The surfactant addition altered these interactions slightly, with CTAB reducing the density of Cl − around In 3+ and SDS positively interacting with In 3+ at 297 K and in a Sn 2+ :In 3+ 1:1. As SDS interacted more with In 3+ ions, the electrodeposition times varied between 4965 s and 75,541 s. SEM images revealed temperature- and potential-dependent changes in film morphology, changing from globular to smooth. CTAB and SDS additions led to uniform coating in Sn 2+ : In 3+ solutions. For the 1:1 ratio at −1.4 V, there were no significant changes (between 75 and 77 %) in the percentage of Sn deposited with the use of surfactants at 297 K. At 343 K, the surfactant-free coating exhibited 69 % Sn, CTAB facilitated the Sn deposition, increasing the percentage to 92 %. At the same time, the presence of the SDS resulted in 79 % Sn. Similar behavior was obtained for −1.0 V. For 1:4 at −1.0 V at 297 K, 35 % of Sn was observed without surfactant, 29 % with CTAB, and 33 % with SDS. At 343 K, there was an increase in Sn content for 42 %, 49 % and 60 %, indicating the positive influence of the temperature, respectively. At −1.4 V, however, there was no observed influence on the Sn percentages without surfactant. With CTAB (between 29 and 34 %) at 297 and 343 K. At these temperatures, the addition of SDS promoted a higher content of Sn, increasing to 56 % and 43 %, respectively.
chemistry, physical