Abstract:The colored bilayer radiative cooling coatings consist of a top layer containing SiO2 microspheres and phosphors and a TiO2‐based white bottom layer, where the SiO2 microspheres can modify the electromagnetic environment of the phosphors and hence accelerate their spontaneous emission rate through Purcell effect. The field test shows that the colored coatings can achieve subambient cooling with temperature drops of up to 1.5 °C. Passive daytime radiative cooling has emerged as a promising green technology for the thermal management of buildings, vehicles, textiles, and electronics. Typically, both high solar reflectance and high thermal emissivity are prerequisites to achieve sufficient daytime cooling. However, colored radiative cooling materials are facing the dilemma of introducing visible light absorption, leading to challenges in balancing cooling and aesthetic demands. Here, three colored bilayer radiative cooling coatings, each comprised of a white base layer and a colored top layer with fluorescence enhancement are fabricated. Three phosphors (Sr2Si5N8:Eu2+, Y3Al5O12:Ce3+, and (Ba,Sr)SiO4:Eu2+) are employed with respective photoluminescence quantum yields (PLQYs) of 81%, 95.8%, and 91.0% as the colored pigment in the top layer. To mitigate the contradiction between coloration and solar reflectance, SiO2 microspheres are introduced into the top layer and utilize their Mie‐resonance‐based multiple scattering to increase the photoluminescent (PL) properties of the phosphors, which jointly boosts the effective solar reflectance (ESR) of the top layer. As a result, the three bilayer coatings exhibit soft colors while achieving subambient cooling with temperature drops of up to 1.5 °C. This fluorescence‐enhancement strategy may pave the way for preparing highly efficient radiative cooling coatings with tunable colors.

Photonic-Structure Colored Radiative Coolers for Daytime Subambient Cooling

Sub-ambient full-color passive radiative cooling under sunlight based on efficient quantum-dot photoluminescence

Scalable Colored Subambient Radiative Coolers Based on a Polymer-Tamm Photonic Structure

Effective, Angle-Independent Radiative Cooler Based on One-Dimensional Photonic Crystal

Polyethylene terephthalate-based colored emitters for efficient daytime radiative cooling

Free-standing, colored, polymer film with composite opal photonic crystal structure for efficient passive daytime radiative cooling

Structurally Colored Photonic Crystal Biomimetic Microstructures for Daytime Radiative Cooling

Colored emitters with silica-embedded perovskite nanocrystals for efficient daytime radiative cooling

Scalable and paint-format colored coatings for passive radiative cooling

Iridescent Daytime Radiative Cooling with No Absorption Peaks in the Visible Range

Fundamentals, Materials, and Applications for Daytime Radiative Cooling

Full Daytime Sub-ambient Radiative Cooling with High Figure of Merit in Commercial-like Paints

Selective spectral absorption of nanofibers for color-preserving daytime radiative cooling

Fluorescence‐Enabled Colored Bilayer Subambient Radiative Cooling Coatings

Vivid Colored Cooling Structure Managing Full Solar Spectrum via Near-Infrared Reflection and Photoluminescence

Subambient daytime radiative cooling of vertical surfaces

Efficient full-color daytime radiative cooling with diffuse-reflection-dominant cholesteric liquid crystals

Thin film-based colorful radiative cooler using diffuse reflection for color display

Creating an Eco‐Friendly Building Coating with Smart Subambient Radiative Cooling

Mechanically Robust and Spectrally Selective Convection Shield for Daytime Subambient Radiative Cooling

A novel aqueous scalable eco-friendly paint for passive daytime radiative cooling in sub-tropical climates