Mechanically Robust and Flexible Perovskite Solar Cells via a Printable and Gelatinous Interface
Tangyue Xue,Gangshu Chen,Xiaotian Hu,Meng Su,Zengqi Huang,Xiangchuan Meng,Ze Jin,Jiale Ma,Yiqiang Zhang,Yanlin Song
DOI: https://doi.org/10.1021/acsami.1c00813
2021-04-22
Abstract:Dramatic development in perovskite solar cells (PSCs) and the widespread application of wearable electronics have attracted extensive research in the area of large-scale flexible solar power sources based on PSCs. Manufacturing of flexible PSCs by printing is considered to be one of the most potential methods. However, it is still a great challenge to print large-area uniform hole transport layers (HTLs) on a rough and soft plastic substrate to achieve flexible PSCs with high efficiency and good stability. Herein, we synthesized a viscous poly(3,4-ethylene dioxythiophene):graphene oxide (PEDOT:GO) gel and then blade-coated the gel by high-speed shearing to achieve high-quality HTLs with scalable size. The glued HTLs exhibit high viscosity, electrical conductivity, and mechanical flexibility, which enhance the adhesive ability and protect the brittle ITO electrode and perovskite crystals. Due to the gelatinous HTLs, we achieved an optimal efficiency of the flexible PSCs (1.01 cm<sup>2</sup>) of 19.7%, while that of the large-area flexible perovskite module (25 cm<sup>2</sup>) exceeded 10%. This is the highest efficiency for reported flexible MAPbI<sub>3</sub> PSCs (1.01 cm<sup>2</sup>). Furthermore, the efficiency retention of the PSCs remains over 85% after 5000 bending cycles, which is of great significance for the practical application of PSCs in portable and wearable electronics.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c00813?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c00813</a>.The optical picture and rheological properties of PEDOT:PSS and GO composites ink with three different combined conditions of ultrasonication, stirring, and ultrasonication disruption; rheological properties of the solution after adding different proportions of GO (1–20 mg mL<sup>–1</sup>); temperature-dependent viscoelasticity and the viscous properties of the PEDOT:GO gel; transmittance spectra, X-ray photoelectron spectroscopy (XPS) spectra S 2p, ultraviolet photoelectron spectroscopy (UPS), and the sheet resistance of GO, PEDOT:PSS, and PEDOT:GO three HTLs; optical and AFM microscopic morphology of the large-area PEDOT:GO gel interface layer (4 × 4 cm<sup>2</sup>) blade coating on the PET film; surface SEM images, grain size distribution, 2D X-ray diffraction (2D-XRD), and steady-state PL spectra of perovskite films on GO, PEDOT:PSS, and PEDOT:GO interface layers; SEM images of GO, PEDOT:PSS, and PEDOT:GO three HTLs, the MAPbI<sub>3</sub> films and the corresponding sheet resistance change bent with 3000 cycles within a curvature radius form flat to 5 mm; finite-elements simulation model, the stress distribution of each layer, and the Young's modulus of the flexible PSCs with PEDOT:PSS and PEDOT:GO interface layer; <i>J</i>–<i>V</i> curves of the PSCs based on GO HTLs; long-term stability of flexible PSCs based on three HTLs (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c00813/suppl_file/am1c00813_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology