Abstract:Metal halide perovskites have emerged as one of the most promising materials for photovoltaics (PVs), with power conversion efficiency of over 22% already demonstrated. In order to compete with traditional crystalline silicon PV, cost and stability are equally important issues that need to be considered besides efficiency. Copper thiocyanate (CuSCN) is an interesting candidate to be used as an inexpensive, thermally stable p‐type charge conducting material in perovskite solar cells. Here, we report 13% efficient perovskite solar cells employing CuSCN as the hole‐transport material. We compare the stability of cells employing CuSCN with those employing the archetypical organic hole‐transporter 2,2′,7,7′‐Tetrakis (N,N‐di‐p‐methoxyphenyl‐amine) 9,9′‐Spirobifluorene (Spiro‐OMeTAD), under elevated temperature in ambient atmosphere. Surprisingly, we find that the devices employing CuSCN degrade faster under elevated temperatures than the devices employing Spiro‐OMeTAD. We discover that an interfacial degradation mechanism occurs at the heterojunction between the perovskite absorber and the CuSCN, even in a dry nitrogen atmosphere, identifying the presence of a critical instability. Interestingly, with the additional coating of the completed cells with a thin film of insulating poly(methyl methacrylate) (PMMA), functioning as a rudimentary “on‐cell” encapsulation, we significantly alleviate this issue and deliver efficient perovskite solar cells which survive for more than 1000 hours at 85 °C in air with only 25% degradation in performance. Beyond identifying a critical area to address in order to enable CuSCN to be useful for long term operation in perovskite solar cells, our findings indicate that the role of the “encapsulant” is to both keep the environment out, and keep degradation products within the cell.

Inverted planar heterojunction perovskite solar cells with high ultraviolet stability

Comprehensive Understanding of Heat-Induced Degradation of Triple-Cation Mixed Halide Perovskite for a Robust Solar Cell

Stabilizing n-type hetero-junctions for NiOx based inverted planar perovskite solar cells with an efficiency of 21.6%

Mitigating the Heterointerface Driven Instability in Perovskite Photovoltaics

Improving Ultraviolet Stability of Perovskite Solar Cells via Singlet Fission Down‐Conversion

Strong-bonding hole-transport layers reduce ultraviolet degradation of perovskite solar cells

Efficient Inverted Planar Perovskite Solar Cells Using Ultraviolet/Ozone‐Treated NiOx As the Hole Transport Layer

Stability Issue of Perovskite Solar Cells under Real‐World Operating Conditions

Unraveling the Modification Effect at NiOx/perovskite interfaces for Efficient and Stable Inverted Perovskite Solar Cells

Low‐Temperature Solution‐Processed CuCrO2 Hole‐Transporting Layer for Efficient and Photostable Perovskite Solar Cells

Stability Issues on Perovskite Solar Cells

Identification and Mitigation of a Critical Interfacial Instability in Perovskite Solar Cells Employing Copper Thiocyanate Hole‐Transporter

Planar MgxZn1-xO-based Perovskite Solar Cell with Superior Ultraviolet Light Stability

UV‐Inert ZnTiO3 Electron Selective Layer for Photostable Perovskite Solar Cells

Efficient Perovskite Solar Cell Modules with High Stability Enabled by Iodide Diffusion Barriers

Long-term operating stability in perovskite photovoltaics

Stability-limiting heterointerfaces of perovskite photovoltaics

Large-Area 23%-Efficient Monolithic Perovskite/Homojunction-Silicon Tandem Solar Cell with Enhanced UV Stability Using Down-Shifting Material

A bilayer conducting polymer structure for planar perovskite solar cells with over 1,400 hours operational stability at elevated temperatures

Stability-enhanced perovskite heterointerfaces and solar cells via strongly anchored and sterically hindered ligands

Eliminating Light-Soaking Instability in Planar Heterojunction Perovskite Solar Cells by Interfacial Modifications.