Electrocatalytic Degradation of Rhodamine B on the Sb-Doped SnO 2 /Ti Electrode in Alkaline Medium

Dongli Deng,Ying Li,Mingzhu Wu,Yang Song,Qiongjian Huang,Yiqin Duan,Yu Chang,Yangyang Zhao,Chunling He

DOI: https://doi.org/10.1021/acsomega.3c08391

IF: 4.1

2023-12-26

ACS Omega

Abstract:To realize efficient electrocatalytic degradation of organic compounds in alkaline wastewater, an Sb-doped SnO(2)/Ti electrode was fabricated and employed for the removal of Rhodamine B (RhB), and the electrocatalytic oxidation performance of this electrode was assessed in an alkaline medium. In an alkaline solution (pH 11), the complete fading of 50 mg·L^(-1) RhB could be achieved after 150 min of degradation, the removal efficiency of the chemical oxygen demand reached 56.1% at 300 min, and...

chemistry, multidisciplinary

What problem does this paper attempt to address?

This paper aims to solve the problem of effective electro - catalytic degradation of organic compounds in alkaline wastewater, especially rhodamine B (RhB). Specifically, the researchers developed an antimony - doped tin dioxide/titanium electrode (Sb - doped SnO₂/Ti) and evaluated its electro - catalytic oxidation performance for RhB in alkaline media. The main objectives of the paper include:

1. **Improve degradation efficiency**: In an alkaline solution with a pH value of 11, complete degradation of 50 mg·L⁻¹ RhB within 150 minutes was achieved, and the chemical oxygen demand (COD) removal rate reached 56.1% within 300 minutes.

2. **Kinetic study**: The degradation process of RhB was verified by the pseudo - first - order reaction kinetic model, indicating that diffusion plays a dominant role in the degradation process.

3. **Mechanism exploration**: The role of hydroxyl radicals (·OH) in RhB degradation was studied, and it was found that ·OH is the main active species and can effectively degrade RhB.

4. **Material characterization**: Techniques such as scanning electron microscopy (SEM), X - ray diffraction (XRD), X - ray photoelectron spectroscopy (XPS) and cyclic voltammetry (CV) were used to analyze the morphological, structural and activity changes of the electrode before and after use.

5. **Practical application**: The application potential of the Sb - doped SnO₂/Ti electrode in treating actual dye wastewater was verified, and the results showed that the electrode has good reusability and stability.

### Abstract
In order to achieve effective electro - catalytic degradation of organic compounds in alkaline wastewater, an antimony - doped tin dioxide/titanium electrode (Sb - doped SnO₂/Ti) was prepared and used to remove rhodamine B (RhB), and the electro - catalytic oxidation performance of this electrode in alkaline media was evaluated. In an alkaline solution with a pH value of 11, 50 mg·L⁻¹ RhB was completely degraded within 150 minutes, the chemical oxygen demand (COD) removal rate reached 56.1% within 300 minutes, and the degradation process of RhB conformed to the pseudo - first - order reaction kinetic model. Under the attack of hydroxyl radicals, part of RhB was degraded into low - molecular - weight organic acids, and the degradation was achieved through N - demethylation and destruction of the conjugated chromophore. The morphological, structural and activity changes of the Sb - doped SnO₂/Ti electrode before and after use were investigated by using multiple techniques (such as scanning electron microscopy, X - ray diffraction, X - ray photoelectron spectroscopy and cyclic voltammetry). The Sb - doped SnO₂/Ti electrode can be mass - produced, each electrode can be reused 8 times without a significant decrease in degradation ability, and the leaching amount of antimony is far below the national standard. In addition, an electrochemical oxidation experiment of a dye wastewater sample was carried out, and the results showed that the electrochemical oxidation technology is very promising in treating alkaline dye wastewater using the Sb - doped SnO₂/Ti electrode.