Mechanisms of Electron-Beam-Induced Damage in Perovskite Thin Films Revealed by Cathodoluminescence Spectroscopy

Chuanxiao Xiao,Zhen Li,Harvey Guthrey,John Moseley,Ye Yang,Sarah Wozny,Helio Moutinho,Bobby To,Joseph J. Berry,Brian Gorman,Yanfa Yan,Kai Zhu,Mowafak Al-Jassim
DOI: https://doi.org/10.1021/acs.jpcc.5b09698
2015-11-18
The Journal of Physical Chemistry C
Abstract:Electron-beam-induced damages in methylammonium lead triiodide (MAPbI3) perovskite thin films were studied by cathodo­luminescence (CL) spectroscopy. We find that high-energy electron beams can significantly alter perovskite properties through two distinct mechanisms: (1) defect formation caused by irradiation damage and (2) phase transformation induced by electron-beam heating. The former mechanism causes quenching and broadening of the excitonic peaks in CL spectra, whereas the latter results in new peaks with higher emission photon energy. The electron-beam damage strongly depends on the electron-beam irradiation conditions. Although CL is a powerful technique for investigating the electronic properties of perovskite materials, irradiation conditions should be carefully controlled to avoid any significant beam damage. In general, reducing acceleration voltage and probing current, coupled with low-temperature cooling, is more favorable for CL characterization and potentially for other scanning electron-beam-based techniques as well. We have also shown that the stability of perovskite materials under electron-beam irradiation can be improved by reducing defects in the original thin films. In addition, we investigated effects of electron-beam irradiation on formamidinium lead triiodide (FAPbI3) and CsPbI3 thin films. FAPbI3 shows similar behavior as MAPbI3, whereas CsPbI3 displays higher resistance to electron-beam damage than its organic–inorganic hybrid counterparts. Using CsPbI3 as a model material, we observed nonuniform luminescence in different grains of perovskite thin films. We also discovered that black-to-yellow phase transformation of CsPbI3 tends to start from the junctions at grain boundaries.
What problem does this paper attempt to address?