Abstract:Zircon (ZrSiO 4 ) ceramics are candidate waste form for immobilizing actinides. However, ZrSiO 4 with single phase suffers from the low actinides solubility. Herein, 0.2Zr 1- a Nd a O 2- a /2 /Zr 1- b Nd b SiO 4- b /2 (0≤ a + b ≤ 0.3) multiphase ceramics were fabricated and their actinides immobilization ability and aqueous stability were evaluated. The evolutions of phase and microstructure affected by Nd doping were investigated. 0.2Zr 1- a Nd a O 2- a /2 /Zr 1- b Nd b SiO 4- b /2 ceramics with 0≤ a + b ˂0.1 exhibited monoclinic ZrO 2 , tetragonal ZrO 2 and ZrSiO 4 mixed phases, while monoclinic ZrO 2 , tetragonal ZrO 2 , ZrSiO 4 and Nd 2 Si 2 O 7 phases with 0.1≤ a + b ≤ 0.3. The increase of lattice volume revealed the successful lattice immobilization of Nd by ZrO 2 /ZrSiO 4 . Due to synergistic immobilization effect, the Nd immobilization capacity of ZrO 2 /ZrSiO 4 is up to 10 at%, which is higher than that of single-phase ZrSiO 4 (4 at%). Furthermore, the obtained ceramics waste form exhibited good compactness and excellent aqueous stability. The results indicated that zirconia/zircon multiphase ceramics can be a potential candidate waste form for actinides.

High capacity synergistic immobilization of simulated trivalent actinides by zirconia/zircon multiphase ceramics