Abstract:This study used the roto-evaporation technique to engineer a 6 mm three-layer polyurethane vascular graft (TVG) that mimics the architecture of human coronary artery native vessels. Two segmented polyurethanes were synthesized using lysine (SPUUK) and ascorbic acid (SPUAA), and the resulting materials were used to create the intima and adventitia layers, respectively. In contrast, the media layer of the TVG was composed of a commercially available polyurethane, Pearlbond 703 EXP. For comparison purposes, single-layer vascular grafts (SVGs) from individual polyurethanes and a polyurethane blend (MVG) were made and tested similarly and evaluated according to the ISO 7198 standard. The TVG exhibited the highest circumferential tensile strength and longitudinal forces compared to single-layer vascular grafts of lower thicknesses made from the same polyurethanes. The TVG also showed higher suture and burst strength values than native vessels. The TVG withstood up to 2087 ± 139 mmHg and exhibited a compliance of 0.15 ± 0.1%/100 mmHg, while SPUUK SVGs showed a compliance of 5.21 ± 1.29%/100 mmHg, akin to coronary arteries but superior to the saphenous vein. An indirect cytocompatibility test using the MDA-MB-231 cell line showed 90 to 100% viability for all polyurethanes, surpassing the minimum 70% threshold needed for biomaterials deemed cytocompatibility. Despite the non-cytotoxic nature of the polyurethane extracts when grown directly on the surface, they displayed poor fibroblast adhesion, except for SPUUK. All vascular grafts showed hemolysis values under the permissible limit of 5% and longer coagulation times.

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop a small - caliber vascular graft capable of imitating the structure of the human coronary artery and evaluate its mechanical properties and biocompatibility. Specifically, the researchers used the roto - evaporation method to fabricate three - layer and single - layer small - caliber polyurethane vascular grafts, and compared the performance of these grafts with single - layer grafts in terms of mechanical properties (such as circumferential tensile strength, longitudinal force, suture strength, and burst strength) and biocompatibility (such as cytocompatibility and hemocompatibility) through a series of tests. ### Main research questions: 1. **Developing three - layer small - caliber vascular grafts**: The researchers aim to fabricate a three - layer small - caliber vascular graft with a different polyurethane material for each layer using the roto - evaporation method to simulate the three - layer structure of the human coronary artery (intima, media, and adventitia). 2. **Comparing the performance of three - layer and single - layer grafts**: The researchers hope to experimentally compare the differences between three - layer grafts and single - layer grafts (using a single polyurethane material or a mixture of three polyurethane materials) in terms of mechanical properties and biocompatibility. 3. **Evaluating mechanical properties**: Evaluate the circumferential tensile strength, longitudinal force, suture strength, and burst strength of the grafts according to the ISO 7198 standard. 4. **Evaluating biocompatibility**: Evaluate the biocompatibility of the grafts through cytocompatibility tests (such as indirect cytotoxicity tests) and hemocompatibility tests (such as hemolysis rate and clotting time). ### Research background: Cardiovascular diseases (CVDs) are the leading cause of death globally, especially during the COVID - 19 pandemic, where complications in the cardiovascular system have increased patient mortality. Coronary artery bypass grafting (CABG) is the gold - standard surgery for treating complex multi - vessel coronary artery disease, but the availability and quality of autologous vascular grafts are limited, so there is a need to develop synthetic vascular grafts as an alternative. Currently, the clinical effectiveness of small - caliber (≤6 mm) vascular grafts is poor, mainly due to their low patency rate, which limits their application in coronary artery bypass grafting. Polyurethane, as a multi - functional biomaterial, has great potential for application in the cardiovascular field, but its long - term stability and safety still need further study. ### Research methods: 1. **Material preparation**: The researchers synthesized two segmented polyurethanes (SPUUK and SPUAA) and used a commercial polyurethane (Pearlbond 703 EXP) as the intermediate - layer material. 2. **Graft fabrication**: Different layers of polyurethane materials were successively deposited on a glass rod by the roto - evaporation method to form a three - layer vascular graft. 3. **Mechanical property testing**: According to the ISO 7198 standard, the grafts were tested for circumferential tensile strength, longitudinal force, suture strength, and burst strength. 4. **Biocompatibility testing**: The biocompatibility of the grafts was evaluated through cytocompatibility and hemocompatibility tests. ### Expected results: The researchers hope that the three - layer vascular graft can be superior to the single - layer graft in terms of mechanical properties and biocompatibility, thus providing new ideas and methods for the development of small - caliber vascular grafts.

A Comparison of Three-Layer and Single-Layer Small Vascular Grafts Manufactured via the Roto-Evaporation Method

Improving the hemocompatibility of a porohyperelastic layered vascular graft using luminal reversal microflows

Evaluation of human umbilical vein endothelial cells growth onto heparin-modified electrospun vascular grafts

Evaluation of properties for Carbothane™ 3575A-based electrospun vascular grafts in vitro and in vivo

A compliant and biomimetic three-layered vascular graft for small blood vessels

Manufacture of small calibre quadruple lamina vascular bypass grafts using a novel automated extrusion-phase-inversion method and nanocomposite polymer

Development of small-diameter vascular grafts using PCL/PLA/gelatin/PVA/hyaluronic acid nanofibers containing VEGF/enoxaparin

Biodegradable, Self-Reinforcing Vascular Grafts for In Situ Tissue Engineering Approaches

Extruded poly (glycerol sebacate) and polyglycolic acid vascular graft forms a neoartery

The Preparation and Performance of a New Polyurethane Vascular Prosthesis

Optimization of Electrospun Bilayer Vascular Grafts through Assessment of the Mechanical Properties of Monolayers

A New Polyurethane/Heparin Vascular Graft for Small-Caliber Vein Repair

[Assessment of the Mechanical Properties and Biocompatibility of a New Electrospun Polyurethane Vascular Prosthesis].

Fabrication and mechanical characterization of near field electrospun bioresorbable vascular grafts with fibrous architecture mimicking the arterial extracellular matrix

A novel hybrid silk-fibroin/polyurethane three-layered vascular graft: towards in situ tissue-engineered vascular accesses for haemodialysis

A Polyurethane-based Hydrophilic Elastomer with Multi-biological Functions for Small-diameter Vascular Grafts

Design and Comprehensive Assessment of a Biomimetic Tri-Layer Tubular Scaffold Via Biodegradable Polymers for Vascular Tissue Engineering Applications

Tissue-Engineered Vascular Graft with Co-Culture of Smooth Muscle Cells and Human Endothelial Vein Cells on an Electrospun Poly(lactic-co-glycolic acid) Microtube Array Membrane

Immunomodulatory Porous Regenerative Scaffolds for Vascular Engineering

Preparation and characterization of a polyvinyl alcohol/polyacrylamide hydrogel vascular graft reinforced with a braided fiber stent

One-Pot Covalent Grafting of Gelatin on Poly(Vinyl Alcohol) Hydrogel to Enhance Endothelialization and Hemocompatibility for Synthetic Vascular Graft Applications.