Multifunctional properties of sonochemically in-situ synthesized and incorporated ZnO/ZnO–SiO2 nanomaterials in cotton fabric

Pranita Magadum,Abhishek Chavan,Shivaji Tayade,Ajit Kamble,Kiran Kumar K. Sharma
DOI: https://doi.org/10.1007/s11696-024-03390-w
IF: 2.146
2024-04-30
Chemical Papers
Abstract:Zinc oxide (ZnO) and zinc oxide-silicon dioxide (ZnO-SiO 2 ) nanomaterials were successfully incorporated into cotton fabric yarn using a single step sonochemical method in aqueous medium. The resulting cotton fabrics were evaluated for the ultraviolet (UV) blocking properties using ultraviolet-diffused reflectance spectroscopy (UV-DRS), wetting studies measured by contact angle, and flammability test by vertical flame test (VFT) method. The hydrodynamic diameter of the incorporated nanomaterials was in the range of 30–600 nm. 1, 2, 3, 4-butanetetracarboxylic acid (BTCA) was used as a cross-linking agent between the free -OH groups of the cotton fabric yarns. The results of ZnO-SiO 2 incorporated cotton fabric exhibited 8.8% enhancement in UV-B blocking, wettability of 124.5° and flame time of 9 ± 1 s as compared to control cotton fabric. The UV blocking by ZnO-SiO 2 incorporated cotton fabric was retained even after 10 washing cycles. The study highlights a single step method for the simultaneous in-situ synthesis and incorporation nanomaterials in cotton fabrics sonochemically as an alternative method for enhanced multifunctionality.
chemistry, multidisciplinary
What problem does this paper attempt to address?