Abstract:Poly(butyl acrylate)/nanosilica (PBA/SiO2) composite particles were prepared by in situ emulsion polymerization initiated by 2,2’-azobis(2-amidinopropane)dihydrochloride (AIBA) initiator adsorbed on the surface of nanosilica particles. The morphology of the composite particles was observed by transmission electron microscopy, and the combination grade of PBA latex particles with SiO2 particles was characterized by centrifugation/re-dispersion and HF etching experiments. The results show that the PBA/SiO2 composite particles exhibit the raspberry-like morphology with most SiO2 particles aggregated at the surface of PBA latex particles. When the mass fraction of SiO2 in the composite particles is in the range of 14.6% to 22.6%, more than 60% SiO2 particles are enriched on the surface of composite particles, and about 30% SiO2 particles are encapsulated in the inner of composite particles. The results also show that the combination strength between SiO2 particles and PBA in the composite particles prepared by in situ emulsion polymerization is stronger than that in the composite particles prepared by direct mixing of PBA latex (prepared by using AIBA as initiator) and SiO2 dispersion. It was considered that, via the ATBA adsorbed on the surface of SiO2 particles, the PBA chains are anchored onto SiO2 particles during in situ emulsion polymerization, the hydrophilicity/hydrophobicity of SiO2 particles and compatibility of SiO2 with PBA vary with the amount of anchored PBA, these lead to the above distribution manner of SiO2 particles in the composite latexes and the morphology of the resultant composite particles.

Synthesis of ultrahigh molecular weight poly(butyl acrylate) in the presence of palladium nanoparticles

Polymorphic Crystallization of Poly(Butylene Adipate) and Its Copolymer: Effect of Poly(Vinyl Alcohol)

Neutral Pd(Ii) and Ni(Ii) Acetylide Complexes As Single-Component Initiators for Polymerizations of Butyl Methacrylate and Acrylates

Facile Synthesis of Ultrahigh Molecular Weight Poly(Methyl Methacrylate) by Organic Halides in the Presence of Palladium Nanoparticles

Synthesis of Semi-Aromatic Copolyester with High Molecular Weight

Ab initio RAFT emulsion polymerization of butadiene using the amphiphilic poly(acrylic acid-b-styrene) trithiocarbonate as both surfactant and mediator

Emulsion Copolymerization of Butyl Acrylate with Cationic Monomer Using Interfacial Redox Initiator System

Synthesis of Ultrahigh Molecular Weight Poly (Trifluoroethyl Methacrylate) Initiated by the Combination of Palladium Nanoparticles with Organic Halides

Neutral Pd(II) and Ni(II) Acetylide Catalysts for the Polymerization of Methyl Methacrylate

Polymerization of 1-chloro-2-phenylacetylene derivatives by using a Brookhart-type catalyst

Synthesis and Characterization of Poly(butyl Acrylate)/silica and Poly(butyl Acrylate)/silica/poly(methyl Methacrylate) Composite Particles

Reverse Atom Transfer Radical Polymerization Of Methyl Acrylate Using Aibn As The Initiator Under Heterogeneous Conditions

Polymerization of 1-chloro-2-benzaldehyde-acetylene using an NHC-Pd/AgOTf catalyst and post-polymerization modification

Transition Metal Acetylide Catalysts for Polymerization of Alkynes

Morphology and Formation Mechanism of Poly(butyl Acrylate)/nanosilica Composite Particles Prepared by in Situ Emulsion Polymerization

Synthesis of Ultrahigh Molecular Weight Poly(methyl Methacrylate) via the Polymerization of MMA Initiated by the Combination of Palladium Carboxylates with Thiols

Bulk Polymerization of Acrylic Acid Using Dielectric-Barrier Discharge Plasma in a Mesoporous Material.

Synthesis of Poly(isobutyl-P-methylstyrene-g-tert-butyl Acrylate) by Combination of Cationic Polymerization and ATRP in CH_2Cl_2 Solution

A Facile Method to Prepare Polypropylene/poly(butyl Acrylate) Alloy Via Water–solid Phase Suspension Grafting Polymerization

B(C 6 F 5 ) 3 -based Lewis pair-catalyzed acrylate polymerization: Lewis base effects on pairing interactions

Synthesis and Characterization of PBMA‐b‐PDMS‐b‐PBMA Copolymers by Atom Transfer Radical Polymerization