Abstract:The search for cost-effective and highly active transition-metal-based electrocatalysts is of great importance for overall water splitting to generate clean energy hydrogen. In this work, we present a controllable structural transformation engineering strategy to construct 3D hierarchical CoP porous microscale prism-like superstructure (assembled with nanoflakes) arrays grown on surface-phosphatized Ni foam (CoP/SPNF). Specifically, Zn/Co-based composite arrays with a nanowires@prism hierarchical structure were prepared on Ni foam first. Then, porous Co-based compound arrays with a nanoflakes@prism hierarchical structure were obtained through removing the Zn-based compound by alkaline etching. Finally, CoP arrays were produced through phosphatization of the prepared Co-based array precursor, using NaH2PO2·H2O as the P source. The fabricated CoP/SPNF electrocatalyst exhibits impressive bifunctional performance for the hydrogen evolution reaction (HER, overpotential of 45 mV at 10 mA cm-2) and oxygen evolution reaction (OER, overpotential of 215 mV at 80 mA cm-2) and consequently enables efficient electrolytic water splitting with a low cell voltage of 1.547 V at 30 mA cm-2 and a prominent durability. Versatile CoP with its porous superstructure arrays on surface-phosphatized Ni foam can increase the exposure of electrochemically active sites and render easy contact with the electrolyte, thus facilitating fast electron transport and effective electrolyte diffusion during the electrocatalytic process, as well as promoting the release of product gas bubbles from the electrode. This work provides an effective strategy for the design and preparation of non-noble-metal bifunctional electrocatalysts for overall water splitting electrolysis.

Hierarchical superhydrophilic/superaerophobic CoMnP/Ni 2 P nanosheet-based microplate arrays for enhanced overall water splitting

Hierarchical Ni2P@NiFeAlOx Nanosheet Arrays As Bifunctional Catalysts for Superior Overall Water Splitting

Cobalt Phosphide Nanocage@ferric-Zinc Mixed-Metal Phosphide Nanotube Hierarchical Nanocomposites for Enhanced Overall Water Splitting

MnOx-decorated MOF-derived nickel-cobalt bimetallic phosphides nanosheet arrays for overall water splitting

CoMoP/NiFe-Layered Double-Hydroxide Hierarchical Nanosheet Arrays Standing on Ni Foam for Efficient Overall Water Splitting

One-pot Electrodeposition Synthesis of NiFe-phosphate/phosphide Hybrid Nanosheet Arrays for Efficient Water Splitting

Ni 3 S 2 /Cu–NiCo LDH heterostructure nanosheet arrays on Ni foam for electrocatalytic overall water splitting

Hierarchical Cu3P-based nanoarrays on nickel foam as efficient electrocatalysts for overall water splitting

Plasma-activated Co3(PO4)2 Nanosheet Arrays with Co3+-Rich Surfaces for Overall Water Splitting

Hierarchical structure of amorphous Co–P nanosheets decorated crystalline NiCo2S4 nanorods as a bifunctional catalyst for electrocatalytic water splitting

Co-Ni-Mo phosphides hierarchical nanoarrays as bifunctional electrocatalysts for excellent overall water splitting

CoP Microscale Prism-like Superstructure Arrays on Ni Foam as an Efficient Bifunctional Electrocatalyst for Overall Water Splitting

Carbon-Coated Nickel Phosphide Nanosheets As Efficient Dual-Electrocatalyst for Overall Water Splitting

A Hierarchical MoP Nanoflake Array Supported on Ni Foam: A Bifunctional Electrocatalyst for Overall Water Splitting

Anchoring Ni2P Sheets on NiCo2O4 Nanocone Arrays as Optimized Bifunctional Electrocatalyst for Water Splitting

Hierarchical iron-phosphide@NiCo2O4 nanoneedle arrays for high performance water splitting

A pillar-layered Ni2P-Ni5P4-CoP array derived from a metal-organic framework as a bifunctional catalyst for efficient overall water splitting

Amorphous-crystalline coupling CoS/NixPy/Fe-Ni3S2 heterostructure nanoplate array on NF for efficient overall water splitting

Controllable Synthesis of Flower-Like Mn-Co-P Nanosheets As Bifunctional Electrocatalysts for Overall Water Splitting

Heterostructured bimetallic phosphide nanowire arrays with lattice-torsion interfaces for efficient overall water splitting

Quasi-parallel nickel cobalt phosphide nanosheet arrays as highly efficient electrocatalyst for hydrogen evolution and overall water splitting at large current densities