Insights into the stability of poly(ether urethane) composite membranes containing magnetic nanoparticles

Luiza Madalina Gradinaru,Florica Doroftei,Stelian Vlad

DOI: https://doi.org/10.1016/j.colsurfa.2024.133466

IF: 5.518

2024-02-15

Colloids and Surfaces A Physicochemical and Engineering Aspects

Abstract:The stability and durability of materials are crucial for many applications, especially in the design of scaffold matrices suitable for short or long-term biomedical applications. The objective of this work was to investigate and compare the UV and hydrolytic stability of some magnetic polyurethane (PU) membranes, which could be used as basic polymeric materials for the development of biomedical devices. SEM, ATR-FTIR, XRD, contact angle and mechanical investigations were used to monitor changes in the magnetic PU membranes exposed to UV irradiation and hydrolytic degradation conditions (PBS). According to the degradation results at the investigated exposure parameters, this magnetic-embedded ether-based PU can be considered to have significantly higher overall stability (up to 0.3% and 0.17% mass loss for UV and hydrolytic degradation, respectively). Although evidence of the degradation was found on the polymer's surface using both the UV and hydrolytic methods, it was limited to the polymer's surface regions and did not affect the bulk properties. Some obvious changes were observed, particularly for the UV-irradiated samples, where the hydrophilicity increased due to the appearance of some cracks as well as some hydrophilic groups on the surfaces, resulting in an apparent contact angle value of up to 30 degrees. Thus, the UV and hydrolytic resistance of these PU-based materials should offer multiple opportunities for biomedical applications, especially for the development of devices used to improve the image quality of magnetic resonance imaging investigations.

chemistry, physical