The influence of two types of alkali activators on the microstructure and performance of supersulfated cement concrete: mitigating the strength and carbonation resistance

Yang Zhou,Zechuan Peng,Luchuan Chen,Jiale Huang,Tao Ma

DOI: https://doi.org/10.1016/j.cemconcomp.2021.103947

IF: 9.93

2021-04-01

Cement and Concrete Composites

Abstract:<p>As a low-carbon cementitious material, the supersulfated cement (SSC) is composed of a thimbleful of cement clinkers and massive industry by-products, i. e: gypsum and slag. However, the concrete made from SSC suffers low strength, poor carbonation resistance, inferior frost resistance, etc. In such a scenario, two types of alkali activators (lactates and sodium hydroxyl) were employed to improve the microstructure and mitigate the performance of supersulfated cement concrete. The results indicate that the incorporation of lactates effectively improves mechanical performance, water impermeability, and carbonation resistance of supersulfated cement concrete. However, the addition of sodium hydroxide failed to result in a performance enhancement of SSC concrete. Furthermore, the mercury intrusion porosimetry (MIP), X-ray diffraction (XRD), fourier transform infrared spectroscopy (FT-IR) and scanning electron microscope (SEM) were comprehensively utilized to illustrate the microstructure changes of supersulfated cement concrete. It indicates the hydration degree of supersulfated cement was promoted by the addition of lactates, which refined the pore structure of concrete. A more compact matrix conduces to overall performance enhancement. This work may shed new lights on the microstructure optimization of solid-waste-based binding materials and further promote the application of SSC concrete.</p>

construction & building technology,materials science, composites

What problem does this paper attempt to address?

The problems that this paper attempts to solve are some performance defects faced by supersulfated cement (SSC) concrete in practical applications, especially problems such as low strength, poor carbonation durability, and poor frost resistance. Specifically:

1. **Strength problem**: The early - and late - stage strengths of supersulfated cement concrete are both lower than those of traditional Portland cement concrete.
2. **Carbonation durability problem**: The carbonation depth of supersulfated cement concrete is relatively large, indicating that its resistance to carbon dioxide is weak.
3. **Frost resistance problem**: The performance of supersulfated cement concrete in freeze - thaw cycles is not as good as that of traditional Portland cement concrete.

In order to solve these problems, the researchers introduced two types of alkaline activators (lactate and sodium hydroxide), hoping to improve the mechanical properties and durability of supersulfated cement concrete by improving its microstructure.

### Research methods and results

The researchers carried out experimental verification through the following methods:

- **Material selection**: Different types of raw materials were selected, including steel slag, desulfurized gypsum, ordinary portland cement (OPC), water - reducing agent, fine aggregate (quartz sand) and coarse aggregate (basalt gravel).
- **Adding alkaline activators**: Sodium lactate, potassium lactate and sodium hydroxide were added as alkaline activators respectively, and different experimental groups (Ctrl, SSC - 0, SSC - 1, SSC - 2, SSC - 3) were designed.
- **Testing methods**: A series of testing methods were adopted, including compressive strength test, flexural strength test, carbonation test, chloride ion penetration test, water absorption test, etc.

### Main findings

- **The role of lactate**:
- The addition of sodium lactate and potassium lactate significantly increased the compressive strength and flexural strength of supersulfated cement concrete. In particular, the 28 - day compressive strength was increased by approximately 24.1% and 21.3% respectively.
- Lactate also significantly reduced the carbonation depth of concrete, thereby enhancing carbonation durability.
- Lactate can reduce the initial water absorption rate of concrete, indicating that it helps to optimize the pore structure.

- **The role of sodium hydroxide**:
- Sodium hydroxide failed to significantly increase the compressive strength of concrete, and instead led to a decrease in strength at a later stage.
- Sodium hydroxide failed to improve the carbonation durability and chloride ion penetration performance of concrete.

### Conclusion

This study shows that lactate, as an effective alkaline activator, can significantly improve the mechanical properties and durability of supersulfated cement concrete, while sodium hydroxide fails to achieve the expected effect. This finding provides new ideas for optimizing the microstructure of supersulfated cement concrete and is expected to promote its wide application in engineering.