High optical contrast and radiant heat blocking properties of hierarchically structured electrodes for electrochromic windows

Su-Hua Yang,Jia-Hua Yang,Zhi-Young Chen,Chih-Chieh Ho
DOI: https://doi.org/10.1016/j.jallcom.2021.160762
IF: 6.2
2021-11-01
Journal of Alloys and Compounds
Abstract:<p>To prepare the electrochromic electrode, a hierarchical structure of ZnO nanorods (2s-ZnR) was grown via the two-step hydrothermal process and used to mitigate electron scattering and improve the optical transmittance of the electrodes. Compared to the electrode with 1s-ZnR, a 36.6% increase in ΔT% (an increase from 24.3 to 33.2) along with fast coloring and bleaching processes (time reduced by 0.4 and 0.6 s, respectively) were achieved with the 2s-ZnR structured electrode. When an optimal sp-WO<sub>3</sub> thickness was prepared, the Hier-electrode with a double-hierarchical structure of dip-WO<sub>3</sub>/sp-WO<sub>3</sub>/2s-ZnR exhibited a high Δ<em>T</em>% of 50.8, compared to 41.7 and 33.8 analyzed from the Sput- and Dip-electrodes, respectively. When the voltage was switched, the Hier-electrode responded quickly, with <em>t</em><sub>c</sub> of 12.7 s and <em>t</em><sub>b</sub> of 3.8 s. Moreover, when the heat-irradiation time was extended from 60 to 150 s, the temperature of Hier-electrode only slightly increased by 8.15%. Clearly, the Hier-electrodes exhibit a high contrast ratio, fast response, and high radiant heat blocking capability, which has high potential for smart window applications.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?