Selective nitrogen doping on carbon cloth to enhance the performance of zinc anode

Lei Wang,Guilan Fan,Jiuding Liu,Le Zhang,Meng Yu,Zhenhua Yan,Fangyi Cheng

DOI: https://doi.org/10.1016/j.cclet.2020.08.022

IF: 9.1

2021-03-01

Chinese Chemical Letters

Abstract:<p>Metallic zinc is attractive anode material of rechargeable aqueous Zn-based batteries due to its ambient stability, high volumetric capacity, and abundant reserves. Nonetheless, Zn anodes suffer from issues such as low coulombic efficiency (CE), large polarization and dendrite formation. Herein, uniform Zn electrodeposition is reported on carbon substrates by selective nitrogen doping. Combined experimental and theoretical investigations demonstrate that pyrrolic and pyridinic nitrogen doped in carbon play beneficial effect as zinc-philic sites to direct nucleation and growth of metallic Zn, while negligible effect is observed for graphite nitrogen in Zn plating. The carbon cloth with modified amount of doped pyrrolic and pyridinic nitrogen stabilizes Zn plating/stripping with 99.3% CE after 300 cycles and significantly increases the deliverable capacity at high depth of charge and discharge compared to undoped carbon substrate and Zn foil. This work provides a better understanding of heteroatom doping effect in design and preparation of stable 3D carbon-supported zinc anode.</p>

chemistry, multidisciplinary

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the performance problems of zinc anodes in zinc - based aqueous batteries, especially the problems of low Coulombic efficiency (CE), large polarization phenomenon and dendrite formation. These problems limit the performance and lifespan of zinc anodes in practical applications. Through the method of selectively nitrogen - doped carbon cloth, the authors aim to improve the plating/stripping stability of zinc anodes, enhance their cycle stability and capacity utilization, thereby providing new ideas and technical means for the development of high - performance three - dimensional carbon - supported zinc anodes.

Specifically, the paper studied the influence of different types of nitrogen doping (pyrrolic nitrogen, pyridinic nitrogen and graphitic nitrogen) on the zinc deposition behavior. By combining experimental and density functional theory (DFT) calculation methods, it revealed the mechanism of action of pyrrolic nitrogen and pyridinic nitrogen as "zinc - friendly" sites. These sites can homogenize the nucleation and growth process of zinc, effectively inhibit the formation of dendrites, and further improve the electrochemical performance of zinc anodes.