Abstract:Cracks in typical mortar constructions enhance water permeability and degrade ions into the structure, resulting in decreased mortar durability and strength. In this study, mortar samples are created that self-healed their cracks by precipitating calcium carbonate into them. Bacillus subtilus bacterium (10−7, 10−9 cells/mL), calcium lactate, fine aggregate, OPC-cement, water, and bagasse ash were used to make self-healing mortar samples. Calcium lactates were prepared from discarded eggshells and lactic acid to reduce the cost of self-healing mortars, and 5% control burnt bagasse ash was also employed as an OPC-cement alternative. In the presence of moisture, the bacterial spores in mortars become active and begin to feed the nutrient (calcium lactate). The calcium carbonate precipitates and plugs the fracture. Our experimental results demonstrated that cracks in self-healing mortars containing bagasse ash were largely healed after 3 days of curing, but this did not occur in conventional mortar samples. Cracks up to 0.6 mm in self-healing mortars were filled with calcite using 10−7 and 10−9 cell/mL bacteria concentrations. Images from an optical microscope, X-ray Diffraction (XRD), and a scanning electron microscope (SEM) were used to confirm the production of calcite in fractures. Furthermore, throughout the pre- and post-crack-development stages, self-healing mortars have higher compressive strength than conventional mortars. The precipitated calcium carbonates were primed to compact the samples by filling the void spaces in hardened mortar samples. When fissures developed in hardened mortars, bacteria became active in the presence of moisture, causing calcite to precipitate and fill the cracks. The compressive strength and flexural strength of self-healing mortar samples are higher than conventional mortars before cracks develop in the samples. After the healing process of the broken mortar parts (due to cracking), self-healing mortars containing 5% bagasse ash withstand a certain load and have greater flexural strength (100 kPa) than conventional mortars (zero kPa) at 28 days of cure. Self-healing mortars absorb less water than typical mortar samples. Mortar samples containing 10−7 bacteria cells/mL exhibit greater compressive strength, flexural strength, and self-healing ability. XRD and SEM were used to analyze mortar samples with healed fractures. XRD, FTIR, and SEM images were also used to validate the produced calcium lactate. Furthermore, the durability of mortars was evaluated using DTA-TGA analysis and water absorption tests.

Acoustic Emission Waveform Characterization of Crack Origin In Self-Healing of Mortar Due to Internal Carbonation

Assessment of self-healing behavior of polypropylene fiber-reinforced cement mortar with crystalline admixture: the effects of crack widths, cracking ages, and external conditions

Investigation of Self-Healing Mortars with and without Bagasse Ash at Pre- and Post-Crack Times

Effect of autogenous crack self-healing on mechanical strength recovery of cement mortar under various environmental exposure

Evaluation of the self-healing effect in cement-based materials with embedded cementitious capsules by means of Acoustic Emission techniques

Mechanism of Accelerated Self-Healing Behavior of Cement Mortars Incorporating Triethanolamine: Carbonation of Portlandite

Crack sealing evaluation of self-healing mortar with Sporosarcina pasteurii: Influence of bacterial concentration and air-entraining agent

Simulation of Autogenous Self‐Healing in Lime‐Based Mortars

Self-healing of early age cracks in cement-based materials by mineralization of carbonic anhydrase microorganism

Evaluation of crack closure by ultrasonic wave transmission

Investigating the Self-Healing Performance of Cracked Undersea Constructions

Autogenously self-healable cementitious composite incorporating autolytic mineral microspheres: Hydration regulation and structural alteration

Visual and quantitative evaluation of crack bonding rate of self-healing mortars based on volumetric strain analysis

Synergistic self-healing effect and mechanism of fiber and biological capsule on mortar cracks

Ureolytic MICP-Based Self-Healing Mortar under Artificial Seawater Incubation

Self-healing properties of mortar with crystalline admixture: experimental investigation and parameter optimization

Effect of self-healing in closing cracks from the sulfate attack in Portland, supersulfated and alkali-activated cement

The Effects of Crystalline Admixture on the Self-Healing Performance and Mechanical Properties of Mortar with Internally Added Superabsorbent Polymer

Self-healing cementitious materials containing encapsulated epoxy-montmorillonite-calcium nitrate: evaluating crack-healing performance, mechanical and thermal properties

Assessment of self-healing performance of cement-based materials incorporating ion chelator and industrial wastes

Self-Sealing Process Evaluation Method Using Ultrasound Technique in Cement Composites with Mineral Additives