Abstract:Buried pipelines are widely used, so it is necessary to analyze and study their fracture characteristics. The locations of corrosion defects on the pipe are more susceptible to fracture under the influence of internal pressure generated during material transportation. In the open literature, a large number of studies have been conducted on the failure pressure or residual strength of corroded pipelines. On this basis, this study conducts a fracture analysis on buried pipelines with corrosion areas under seismic loads. The extended finite element method was used to model and analyze the buried pipeline under seismic load, and it was found that the stress value at the crack tip was maximum when the circumferential angle of the crack was near 5° in the corrosion area. The changes in the stress field at the crack tip in the corrosion zone of the pipeline under different loads were compared. Based on the BP algorithm, a neural network model that can predict the stress field at the pipe crack tip is established. The neural network is trained using numerical model data, and a prediction model with a prediction error of less than 10% is constructed. The crack tip characteristics were further studied using the BP neural network model, and it was determined that the tip stress fluctuation range is between 450 MPa and 500 MPa. The neural network model is optimized based on the GA algorithm, which solves the problem of convergence difficulties and improves the prediction accuracy. According to the prediction results, it is found that when the internal pressure increases, the corrosion depth will significantly affect the crack tip stress field. The maximum error of the optimized neural network is 5.32%. The calculation data of the optimized neural network model were compared with the calculation data of other models, and it was determined that GA-BPNN has better adaptability in this research problem.

A study of pipe interacting corrosion defects using the FEM and neural networks

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

Failure Pressure Prediction of Medium to High Toughness Pipe with Circumferential Interacting Corrosion Defects Subjected to Combined Loadings Using Artificial Neural Network

Study on the effect of corrosion defects on VIV behavior of marine pipe using a new defective pipe element

Failure Pressure Prediction of a Corroded Pipeline with Longitudinally Interacting Corrosion Defects Subjected to Combined Loadings Using FEM and ANN

Strength prediction of a steel pipe having a hemi-ellipsoidal corrosion defect repaired by GFRP composite patch using artificial neural network

Predicting the Failure Pressure of Pipelines Containing Nonuniform Depth Corrosion Defects Using the Finite Element Method

An Empirical Equation for Failure Pressure Prediction of High Toughness Pipeline with Interacting Corrosion Defects Subjected to Combined Loadings Based on Artificial Neural Network

Failure Pressure Prediction of High Toughness Pipeline with a Single Corrosion Defect Subjected to Combined Loadings Using Artificial Neural Network (ANN)

Comparative studies for failure pressure prediction of corroded pipelines

Artificial Neural Network-Based Failure Pressure Prediction of API 5L X80 Pipeline with Circumferentially Aligned Interacting Corrosion Defects Subjected to Combined Loadings

Finite Element Modeling of the Failure Behavior of Pipelines Containing Interacting Corrosion Defects

Finite Element Models for the Prediction of the Failure Pressure of Pipelines With Long Corrosion Defects

Numerical Simulation and ANN Prediction of Crack Problems within Corrosion Defects

Failure Pressure Evaluation of Corroded Pipeline Using Semi-Empirical and Finite Element Analysis

Effect of interaction between corrosion defects on failure pressure of thin wall steel pipeline

Reliability assessment of corroded pipeline considering multiple defects interaction based on an artificial neural network method