Abstract:In this paper we present the results on the synthesis of nickel-containing particles from solutions of nickel nitrate under the action of a DC glow discharge at atmospheric pressure in air. The interaction of the plasma with the solution leads to the formation of a colloidal suspension in the anode part of the cell, followed by the formation of agglomerates and precipitation to the bottom of the cell. The composition and surface structure of the resulting powders were studied using scanning electron microscopy, Brunauer–Emmett–Teller analysis, X-ray diffraction analysis, X-ray energy-dispersive spectroscopy, and thermogravimetric analysis. According to the results of dynamic light scattering, particles in solution have two characteristic sizes of the order of 73.5 nm and 1.2 μm. Images obtained on a scanning electron microscope showed that the resulting powders have a well-developed granular structure. X-ray phase analysis of the obtained samples showed the presence of clearly defined reflections, which indicate the crystallinity of the structure of the synthesized powder. Decoding showed that it is β-type nickel hydroxide. The elemental composition of the surface obtained using X-ray energy-dispersive spectroscopy showed the presence of nitrogen in the sample. Therefore, the powders have a complex composition and are a mixture of hydroxide and hydroxonitrate with a ratio of 0.8 Ni(OH)2 : 0.2 Ni(OH)NO3. Thermogravimetric analysis confirms the data obtained using X-ray energy dispersive spectroscopy. High-temperature treatment of the obtained powders leads to the formation of β-type nickel oxide. The specific surface area (Ssp) was calculated using the Brunauer–Emmett–Teller method from the adsorption branch in the range of relative pressures of 0.05–0.20; the total pore volume (Vp) and pore size distribution were calculated from the desorption branch in the range of 0.40–0.99.

Preparation of an ultrafine nickel powder by solid-phase reduction with a NaCl separator agent

Preparation of nickel ultrafine powder and crystalline film by chemical control reduction

Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Preparation of Fine Nickel Powders Via Reduction of Nickel Hydrazine Complex Precursors

Preparation and Characterization of Mono-disperse Spherical Nickel Particles

Preparation of Ultra-Fine Nickel by Electrochemical Milling Method

The Preparation of the Highly Dispersed and Nano-sized Nickel Powders

Preparation of Ni-P Amorphous Alloy Ultrafine Powders

Preparation Methods and Development Tendency of Ultrafine Nickel Powder Applicated in Conductive Pastes

Preparation of nanocrystalline nickel powders through hydrothermal-reduction method

RESEARCH ON PREPARATION OF NICKEL POWDER BY ELECTROLYTIC DEOXIDATION FROM NiO

A STUDY ON THE PREPARATION AND PROPERTIES OF AMORPHOUS NI-P ULTRAFINE PARTICLES

A study on preparation of ultrafine powders of Ni(OH)2 and NiO with different shapes by precipitation transformation method

Study on Preparation of High-Performance Flake Silver Powder by Liquid Phase Reduction

Preparation of hexagonal close-packed nickel nanoparticles via a thermal decomposition approach using nickel acetate tetrahydrate as a precursor

Progress in Preparation of Ultrafine Copper Powder by Chemical Reduction Method

Progress in Preparation and Application of Ultra-fine NiO Powder

The Preparation of an Ultrafine Copper Powder by the Hydrogen Reduction of an Ultrafine Copper Oxide Powder and Reduction Kinetics

PRECIPITATION OF NICKEL-CONTAINING PARTICLES FROM NICKEL NITRATE SOLUTIONS UNDER THE ACTION OF A DIRECT CURRENT GLOW DISCHARGE

The Preparation of Silver-Coated Nickel Powders Via Electroless Plating