Expanded MoSe 2 Nanosheets Vertically Bonded on Reduced Graphene Oxide for Sodium and Potassium-Ion Storage
Shaokun Chong,Xuedong Wei,Yifang Wu,Lan Sun,Chengyong Shu,Qianbo Lu,Yingzhen Hu,Guozhong Cao,Wei Huang,Shaokun Chong,Xuedong Wei,Yifang Wu,Lan Sun,Chengyong Shu,Qianbo Lu,Yingzhen Hu,Guozhong Cao,Wei Huang
DOI: https://doi.org/10.1021/acsami.0c22430
2021-03-14
Abstract:The cost-efficient and plentiful Na and K resources motivate the research on ideal electrodes for sodium-ion batteries (SIBs) and potassium-ion batteries (PIBs). Here, MoSe<sub>2</sub> nanosheets perpendicularly anchored on reduced graphene oxide (rGO) are studied as an electrode for SIBs and PIBs. Not only does the graphene network serves as a nucleation substrate for suppressing the agglomeration of MoSe<sub>2</sub> nanosheets to eliminate the electrode fracture but also facilitates the electrochemical kinetics process and provides a buffer zone to tolerate the large strain. An expanded interplanar spacing of 7.9 Å is conducive to fast alkaline ion diffusion, and the formed chemical bondings (C–Mo and C–O–Mo) promote the structure integrity and the charge transfer kinetics. Consequently, MoSe<sub>2</sub>@5%rGO exhibits a reversible specific capacity of 458.3 mAh·g<sup>–1</sup> at 100 mA·g<sup>–1</sup>, great cyclability with a retention of 383.6 mAh·g<sup>–1</sup> over 50 cycles, and excellent rate capability (251.3 mAh·g<sup>–1</sup> at 5 A·g<sup>–1</sup>) for SIBs. For PIBs, a high first specific capacity of 365.5 mAh·g<sup>–1</sup> at 100 mA·g<sup>–1</sup> with a low capacity fading of 51.5 mAh·g<sup>–1</sup> upon 50 cycles and satisfactory rate property are acquired for MoSe<sub>2</sub>@10%rGO composite. <i>Ex situ</i> measurements validate that the discharge products are Na<sub>2</sub>Se for SIBs and K<sub>5</sub>Se<sub>3</sub> for PIBs, and robust chemical bonds boost the structure stability for Na- and K-ion storage. The full batteries are successfully fabricated to verify the practical feasibility of MoSe<sub>2</sub>@5%rGO composite.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c22430?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c22430</a>.Additional SEM images, TEM image, HRTEM image, EDS mapping images, SAED pattern, XRD patterns, Raman spectra, N<sub>2</sub> adsorption–desorption isotherms, mesoporous size distribution curves, XPS survey spectra, CV profiles and charge/discharge curves for SIBs, comparison of the rate properties of the previously reported MoSe<sub>2</sub>-based materials for SIBs with our work, charge/discharge profiles at different current densities for SIBs, CV profiles and charge/discharge curves for PIBs, CV curves at various scanning rates for PIBs, EIS results, TEM images at different states for SIBs and PIBs, SAED patterns, HRTEM images and XPS spectra at the first fully discharged and charged states for PIBs, and illustration diagram of full batteries, as well as charge/discharge curves and cycling stability of Na<sub>2</sub>Ni[Fe(CN)<sub>6</sub>] and K<sub>2</sub>Ni[Fe(CN)<sub>6</sub>] cathodes in half cell systems (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c22430/suppl_file/am0c22430_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology