Development of g-C3N4 Coated Eggshell Waste-Derived Ca(OH)2 Nanoparticles as a Photocatalyst for the Degradation of Eriochrome Cyanin R with Promising Antibacterial Activity

Abdulaziz Al-Anazi,Ahmed M. El-Khawaga,Changseok Han,Gharieb S. El-Sayyad

DOI: https://doi.org/10.1007/s10904-024-03493-7

IF: 3.518

2024-11-28

Journal of Inorganic and Organometallic Polymers and Materials

Abstract:The present investigation provides a cost-effective approach to the development of nanostructured g-C 3 N 4 coated eggshell waste-derived Ca(OH) 2 nanoparticles as a photocatalyst for the degradation of Eriochrome cyanin R (ECR), and disinfection of pathogenic bacteria. The g-C 3 N 4 /Ca(OH) 2 nanocomposite was characterized via XRD, SEM, EDX, and TEM. XRD patterns and TEM images revealed the successful synthesis of the samples in nanoscale range. The efficacy of the g-C 3 N 4 /Ca(OH) 2 nanocomposite was assessed with different parameters, including solution pH, initial concentration of a targeted contaminant, and loading of the g-C 3 N 4 /Ca(OH) 2 nanocomposite. Notably, 0.01 g of the g-C 3 N 4 /Ca(OH) 2 nanocomposite achieved an impressive 90.0% removal efficiency of ECR at the solution pH of 3.0. When isopropanol was added, the photodegradation of ECR dye by the g-C 3 N 4 /Ca(OH) 2 nanocomposite was decreased (42%), suggesting that the OH⋅ radical was the primary species responsible for degradation. The tested samples are effective against various bacteria, including Eschericia coli (E. coli) and Staphylococcus aureus (S. aureus) . Specifically, the g-C 3 N 4 /Ca(OH) 2 nanocomposite was the most effective combination against S. aureus (13.9 mm ZOI and 12.5 μg/mL MIC), and E. coli (12.4 mm ZOI and 12.5 μg/mL MIC). In reaction mechanism determination, the amount of the synthesized nanomaterials is directly correlated with the quantity of E. coli protein removed, and they were accounted as 22.23, 55.10, and 101.44 μg/mL following incubation with g-C 3 N 4 , Ca(OH) 2 NPs, and g-C 3 N 4 /Ca(OH) 2 nanocomposite, respectively.

polymer science